Search

The nanoparticle spinel ferrites Mg0.5Zn0.5CexLaxFe2-2xO4 (x = 0.0, 0.0125, 0.025, 0.0375, 0.05) were synthesized by mean of co-precipitation method. These magnetic nanoparticles were sintered at 750 °C for 8 h. XRD patterns confirmed the formation of the cubic spinel structure of prepared nanoparticles. The lattice constant of nanoparticle ferrites increased, while crystallite size decreased with doping content (x). Pure ferrite sample has an optical bandgap of 2.61 eV, and it increases from 1.73 to 2.17 eV as concentration (x) is changed from 0.0125 to 0.05. The electrical dc resistivity is of the order of 1010 Ω cm for doping content (x) from 0 to 0.0375 and has a maximum value of 5.48617 × 1012 Ω cm for content x = 0.05. The Curie temperature (Tc) decreased 433–373 K as concentration (x) was increased. The dielectric constant, dielectric loss, and impedance are reduced with the increase of frequency. The dielectric constant, as well as the dielectric loss diminished while impedance increased as doping of cerium and lanthanum, was increased. [ABSTRACT FROM AUTHOR]

Cost-effective and controllable synthesis of M0.25Ni0.15Cu0.25Co0.35Fe2O4 (M2+ = Mg2+, Mn2+, and Cd2+) ferrites via the sol–gel auto-combustion technique. The impact of divalent cations on the structural, dielectric, and optoelectrical properties of ferrites was examined by XRD, FTIR, Raman, LCR, UV–Vis, and two probe I-V measurement techniques. The crystallite size was 52.66 nm, and the minimum specific surface area was observed 5.1507 m2/g for Mg2+ doped NCCF ferrite. The FTIR and Raman analysis also confirmed the substitution of divalent cations (M2+ = Mg2+, Mn2+, and Cd2+) at their respective lattice sites. The maximum energy bandgap was 1.67 eV Mg2+-doped NCCF ferrite as compared to other divalent ion-doped ferrites. The dielectric loss decreased while the ac conductivity increased with increasing frequency, and the minimum values were observed for Mg2+-doped NCCF ferrite. The activation energy was observed maximum for Mg2+-doped NCCF ferrite (0.2234 eV). Due to incredible properties including small specific surface area, large energy band gap, high resistivity, and loss dielectric loss of Mg2+-doped NCCF ferrite have potential applications in different fields. [ABSTRACT FROM AUTHOR]

Cadmium ferrites belong to normal spinel ferrites, and they exhibit interesting electrical, magnetic, and optical properties. The pure and cerium-doped cadmium ferrites CdFe2−xCexO4 (x = 0.0, 0.125, 0.250, 0.375, 0.5) were synthesized by a chemical co-precipitating technique using sodium hydroxide as a co-precipitating agent. The structures and phase purity of fabricated nanomaterials were analyzed by X-ray diffraction (XRD). The crystallite size for all the prepared nanomaterials was in the range of 28–46 nm. The lattice constant and unit cell volume were found to decrease with the increasing concentration of Cerium, which was confirmed by the peak shift in the XRD pattern. The X-ray density for all nano ferrites increased with the enhancement of cerium composition. The resistivity of the nanomaterials has random behavior with the enhancement of cerium composition for a temperature, but the value of resistivity at x = 0.125 has the lowest value and at x = 0.375 has the highest value for almost all temperatures. For specific concentrations, a decreasing trend of resistivity of fabricated materials was found with an increment of temperature. The activation energies were also calculated, and it increased for x = 0.125 and then decreased for all the nanomaterials. For the confirmation of the M–O bonds, FTIR analysis of all the nano ferrites was also performed. The analysis shows a higher frequency absorption band in the range of 531.24–534.84 cm−1. This absorption band confirms that metal oxides are formed in all the synthesized nanoparticles. [ABSTRACT FROM AUTHOR]

Cobalt ferrites have attracted extraordinary attention due to their high coercivity, chemical stability, and mechanical hardness. Lanthanum doped-cobalt ferrites having chemical formula CoLaxFe2-xO4 with composition x = (0.00, 0.015, 0.045, 0.060) were synthesized by chemical co-precipitation method. The prepared samples were characterized by X-ray diffraction (XRD), Fourier-transform infrared spectroscopy (FTIR), Raman spectroscopy, and current-voltage (I-V) technique. The structure of the crystal was analyzed by X-ray diffraction. The crystallite size of nanoparticles was examined in the range of 21–25 nm, and a fluctuating trend was found with the inclusion of La3+ cations. The X-ray diffraction patterns verify the contraction of lattice constant and unit cell volume with the substitution of La3+ cations except for the concentration of x = 0.060. Lattice constant was in the range of 8.34 Å–8.41 Å while unit volume cell was in the range of 580 Å3–596 Å3. The resistivity of all samples was calculated by the application of two probes I-V technique. The maximum resistivity of the order of 81.129 × 105 Ω cm was found for the concentration of x = 0.060 at 723 K which makes it useful for high-frequency gimmicks applications. The resistivity and drift mobility were found inversely related to each other. The inverse relation low-frequency absorption band and high-frequency absorption bands were analyzed by Fourier-transform infrared spectroscopy technique. [ABSTRACT FROM AUTHOR]

Cadmium ferrites belong to normal spinel ferrites, and they exhibit interesting electrical, magnetic, and optical properties. The pure and cerium-doped cadmium ferrites CdFe2−xCexO4 (x = 0.0, 0.125, 0.250, 0.375, 0.5) were synthesized by a chemical co-precipitating technique using sodium hydroxide as a co-precipitating agent. The structures and phase purity of fabricated nanomaterials were analyzed by X-ray diffraction (XRD). The crystallite size for all the prepared nanomaterials was in the range of 28–46 nm. The lattice constant and unit cell volume were found to decrease with the increasing concentration of Cerium, which was confirmed by the peak shift in the XRD pattern. The X-ray density for all nano ferrites increased with the enhancement of cerium composition. The resistivity of the nanomaterials has random behavior with the enhancement of cerium composition for a temperature, but the value of resistivity at x = 0.125 has the lowest value and at x = 0.375 has the highest value for almost all temperatures. For specific concentrations, a decreasing trend of resistivity of fabricated materials was found with an increment of temperature. The activation energies were also calculated, and it increased for x = 0.125 and then decreased for all the nanomaterials. For the confirmation of the M–O bonds, FTIR analysis of all the nano ferrites was also performed. The analysis shows a higher frequency absorption band in the range of 531.24–534.84 cm−1. This absorption band confirms that metal oxides are formed in all the synthesized nanoparticles. [ABSTRACT FROM AUTHOR]