Search

Ceramic foams with significant porosity and robust mechanical properties have received extensive attentions. However, it is still difficult to achieve excellent compressive strength at high porosity levels. In this work, a gelation of foamed boehmite sol method is proposed to settle this issue. The technological parameters during preparation process are systematically investigated. As‐prepared alumina ceramic foams possess unprecedentedly high compressive strength of 34.1‐89.1 MPa at high porosity levels of 66.0%‐87.2%, which is attributed to the present of hierarchical pore structure, small grain size and pore size. This work demonstrates a facile and novel method for the fabrication of high‐performance alumina ceramic foams toward practical applications. [ABSTRACT FROM AUTHOR]

Ultralight ceramic foam materials with high porosity play an important role in increasingly hi‐tech areas due to the combinative merit of ceramic material and highly porous structure. So far, it remains challenging to fabricate alumina ceramic foams with extremely high porosity and high specific surface area that are comparable to aerogel materials by employing a low cost, eco‐friendly and convenient approach. For the first time, we propose the preparation of aerogel‐like ceramic foams with nanoscale cell wall and unprecedentedly high porosity using boehmite sol as both ceramic source and bubble interface stabilizer, based on sol nanoparticles stabilized foams using sodium lauryl sulfate (SDS) as modifier. The obtained ultra‐stable sol foams allow for the achievement of bulk foams with ultrathin cell wall with thickness in the range of 30‐90 nm, super‐high porosity up to 99%, and large specific surface area of 280 m2/g, which is attributed to the well‐organized assembly of nanoparticles at the liquid/air interfaces. This novel foam material demonstrates excellent adsorption ability for polar volatile organic gases (VOCs) due to its extremely high porosity and large specific surface area. Ultralgiht cellular ceramic foams composed of uniformly assembled nanoparticles with nanoscale cell wall. [ABSTRACT FROM AUTHOR]

Three‐dimensional ceramic nanofiber‐assembled materials with large specific surface area and excellent thermal insulation properties are attracting increasing interests for their unique structure and promising applications. In this paper, we propose a facile methodology to fabricate three‐dimensional silicon nitride nanofiber‐knitted ceramic foams via in situ reactive synthesis from silicon foams. Silicon particle‐stabilized foams are fabricated for the first time using long‐chain surfactant cetyltrimethyl ammonium bromide as a hydrophobic modifier. First, the fabrication and stability of silicon foams are investigated. Based on the stable silicon foams, silicon nitride‐based nanofiber‐knitted ceramic foams are synthesized via in situ reactive sintering in nitrogen atmosphere. The novel ceramic foam materials consist of three‐dimensional nanofiber‐assembled strut wall and nanofiber‐spheres in the pores. The diameter of obtained silicon nitride nanofibers ranges from 15 to 100 nm. The unique nanofiber‐knitted foams may have potential applications in specific fields, including catalysis, adsorption, separation, and thermal insulation. [ABSTRACT FROM AUTHOR]

Hierarchical structured porous ceramics have attracted tremendous research interests because of their numerous excellent properties including robust mechanical strength and large surface area. In this work, silicon carbide (SiC)‐based porous ceramics with three levels of pore hierarchy are fabricated from silicon particle‐stabilized foams and a subsequent one‐step calcination after they were embedded with coke. Three‐dimensional (3D) flexible nanofibrous network is adhered and wrapped on cell walls of porous ceramics, which is readily fine‐tuned and tailored by the temperature to provide optimized pore structure. The resultant SiC‐based porous ceramics present a density of 1.03 g/cm3 at a porosity of 72% with a large quantity of hierarchical micro‐ and macropores. This hierarchical structure leads to robust compressive strength (23.52 MPa) and large surface area (64.32 m2/g). The fabrication method is straightforward and sought‐after, providing a facile technical route for advanced hierarchical porous ceramics used in filtration and catalysis fields. [ABSTRACT FROM AUTHOR]

A novel kind of nanowire sponges, namely Si3N4 nanowire‐weaving microspheres, synthesized from a simple, convenient, high‐efficient approach are proposed here. As the reverse template, three‐dimensional foam skeleton structure with uniform pores and ultrathin pore walls is constructed via the effective particle‐stabilized foam method, where the silica sol and carbon black are chosen as the raw materials, providing the sufficient space for the growth of nanowires during the carbothermal reduction reaction process. The formation mechanism of this novel sponge is studied via multiple characterization methods. Si3N4 nanowires formed microspheres possess uniform and curving morphology due to the stable environment for growing via vapor–solid mechanism, leading to the relatively high specific surface area of 86.77 m2/g. Owing to in‐situ oxidation process, micro‐spherical SiO2 nanowire sponges with similar morphology are synthesized, which present diameter in range of 20‐40 nm and specific surface area of 50.47 m2/g. This work provides insights for the design of high‐performance nanowire sponges with promising applications in the filtration, thermal insulators, and catalyst supports fields. [ABSTRACT FROM AUTHOR]

Abstract: A novel method for fabrication of highly porous barium strontium titanate (BST) ceramic foams based on particle‐stabilized foaming method was developed for the first time, in which propyl gallate (PG) was employed as BST particle modifier. The results showed that the stability of wet BST foams closely depends on the pH value and PG concentration, which could be explained by the adsorption behavior of PG on BST particle surface. BST ceramic foams with dense, uniform, and closed pore and defect‐free wall were obtained. The pore size and porosity can be well controlled by adjusting solid loading and sintering temperature. It was revealed that not only sintering temperature but also solid loading significantly influenced the growth of BST grain. The BST ceramic foams exhibited high porosity in the range of 81%‐95%, low dielectric constant in the range of 47‐150, and low dielectric loss below 0.0025. The BST ceramic foams with higher porosity presented a tendency of lower dielectric constant and the fitting results indicated that the natural logarithm of dielectric constant was linear correlated with porosity. [ABSTRACT FROM AUTHOR]