Thin-film La0.58Sr0.4Co0.2Fe0.8O3-δ (LSCF58428) exhibits high oxygen permeability due to its high ionic and electronic conductivity. In order to increase the oxygen flux, a thin-film membrane on a structural substrate is beneficial. Different Ni-based alloys were studied as potential substrate materials. The chemical compositions and thermal expansion coefficients of Nibased alloys were measured in this study. LSCF58428 layers were screen printed on Ni-based alloys and cofired at a high temperature in air. Microstructural and elemental analyses of samples were conducted using a scanning electron microscope and energy-dispersive X-ray spectroscope. X-ray diffraction was used to investigate the phase compositions. The Ni-based alloy, MCrAlY (with M = Ni, Co), with a high Al content showed better chemical compatibility with perovskite material at high temperatures than other Ni-based alloys. A reaction occurred between Sr in the perovskite and the alumina-based surface layer on MCrAlY. However, the reaction zone was found to be stable in mid-term annealing at 800°C in air. Hence, it is expected that this reaction will not prevent application as an oxygen transport membrane. Three different cofiring atmospheres were investigated. Air was found to be the only possible cofiring atmosphere. [ABSTRACT FROM AUTHOR]

Zirconia doped with 3.2–4.2 mol% (6–8 wt%) yttria (3–4YSZ) is currently the material of choice for thermal barrier coating topcoats. The present study examines the ZrO2-Y2O3Ta2O5/Nb2O5 systems for potential alternative chemistries that would overcome the limitations of the 3–4YSZ. A rationale for choosing specific compositions based on the effect of defect chemistry on the thermal conductivity and phase stability in zirconia-based systems is presented. The results show that it is possible to produce stable (for up to 200 h at 1000°-1500°C), single (tetragonal) or dual (tetragonal + cubic) phase chemistries that have thermal conductivity that is as low (1.8–2.8W/m K) as the 3–4YSZ, a wide range of elastic moduli (150–232 GPa), and a similar mean coefficient of thermal expansion at 1000°C. The chemistries can be plasma sprayed without change in composition or deleterious effects to phase stability. Preliminary burner rig testing results on one of the compositions are also presented. [ABSTRACT FROM AUTHOR]