Due to the huge difference in the solubility‐product constants (Ksp) between the precipitates of Lu and Al, the synthesis of lutetium aluminum garnet (Lu3Al5O12, LuAG) nanopowders by coprecipitation method is prone to Lu loss, resulting in the creation of Al2O3 secondary phase. In this work, coprecipitated (Ce0.001Ca0.0015Lu(0.9975+x%))3Al5O12 (x = 0, 0.9, 1.2, 1.5) nanopowders with different starting stoichiometries are synthesized and combined with vacuum pre‐sintering and hot‐isostatic pressing to fabricate scintillating ceramics. The effect of compensated Lu content on the phase composition, microstructure, optical properties, and scintillation performance of ceramics is analyzed. The complete elimination of the secondary phase requires an additional compensation of 1.2% of Lu, which gives the best transmittance in ceramics. When x = 1.5, excessive Lu forms LuAl antisite defect, leading to the decrease of both light yield and intensity of the fast scintillation component. [ABSTRACT FROM AUTHOR]

A green Y5(SiO4)3N:Eu2+ phosphor has been successfully prepared by developing a new SiC reduction-assisted sol-gel method. The valence state of Eu ions was identified with XPS analysis and the photoluminescence spectrum presents a Eu2+ typical broad green emission band. XRD analysis, photoluminescence and excitation measurement, and FTIR test were also carried out, to obtain crystal phase, light emitting, and chemical bonding results. The specific mechanism of SiC reductant in the synthetic process was studied in details. This novel method shows lower equipment requirements and is cost saving. The method can extend applications in synthesizing other silicon-based oxynitrides. [ABSTRACT FROM AUTHOR]