The dissociation of H

Optimizing the use of expensive precious metals is critical to developing sustainable and low-cost processes for heterogeneous catalysis or electrochemistry. Here, we report a synthesis method that yields core-shell Cu-Ru, Cu-Rh, and Cu-Ir nanoparticles with the platinum-group metals segregated on the surface. The synthesis of Cu-Ru, Cu-Rh, and Cu-Ir particles allows maximization of the surface area of these metals and improves catalytic performance. Furthermore, the Cu core can be selectively etched to obtain nanoshells of the platinum-group metal components, leading to a further increase in the active surface area. Characterization of the samples was performed with X-ray absorption spectroscopy, X-ray powder diffraction, and ex situ and in situ transmission electron microscopy. CO oxidation was used as a reference reaction: the three core-shell particles and derivatives exhibited promising catalyst performance and stability after redox cycling. These results suggest that this synthesis approach may optimize the use of platinum-group metals in catalytic applications.

Alloying is a long-established strategy to tailor properties of metals for specific applications, thus retaining or enhancing the principal elemental characteristics while offering additional functionality from the added elements. We propose a similar approach to the control of properties of two-dimensional transition metal carbides known as MXenes. MXenes (Mn+1Xn) have two sites for compositional variation: elemental substitution on both the metal (M) and carbon/nitrogen (X) sites presents promising routes for tailoring the chemical, optical, electronic, or mechanical properties of MXenes. Herein, we systematically investigated three interrelated binary solid-solution MXene systems based on Ti, Nb, and/or V at the M-site in a M2XTx structure (Ti2-yNbyCTx, Ti2-yVyCTx, and V2-yNbyCTx, where Tx stands for surface terminations) showing the evolution of electronic and optical properties as a function of composition. All three MXene systems show unlimited solubility and random distribution of metal elements in the metal sublattice. Optically, the MXene systems are tailorable in a nonlinear fashion, with absorption peaks from ultraviolet to near-infrared wavelength. The macroscopic electrical conductivity of solid solution MXenes can be controllably varied over 3 orders of magnitude at room temperature and 6 orders of magnitude from 10 to 300 K. This work greatly increases the number of nonstoichiometric MXenes reported to date and opens avenues for controlling physical properties of different MXenes with a limitless number of compositions possible through M-site solid solutions.

The ability to stabilize very small Pt crystallites in supported-metal catalysts following harsh treatments is an important industrial problem. Here, we demonstrate that Pt particles can be maintained in the 1- to 2-nm range following multiple oxidation and reduction cycles at 1073 K when the particles are supported on 0.5-nm LaFeO

The two-dimensionally connected metal-organic frameworks (MOFs) Ni3(HIB)2 and Cu3(HIB)2 (HIB = hexaiminobenzene) are bulk electrical conductors and exhibit ultraviolet-photoelectron spectroscopy (UPS) signatures expected of metallic solids. Electronic band structure calculations confirm that in both materials the Fermi energy lies in a partially filled delocalized band. Together with additional structural characterization and microscopy data, these results represent the first report of metallic behavior and permanent porosity coexisting within a metal-organic framework.

Intercalation-type electrodes have now been commonly employed in today's batteries as such materials are capable of storing and releasing lithium reversibly via topotactic transformation, conducive to small structural change, but they have limited interstitial sites to hold Li. In contrast, conversion electrodes feature high Li-storage capacity, but often undergo large structural change during (de)lithiation, resulting in cycling instability. One exception is iron fluoride (FeF

The two-dimensionally connected metal-organic frameworks (MOFs) Ni

Water reduction under two different visible-light ranges (λ > 400 nm and λ > 435 nm) was investigated in gold-loaded titanium dioxide (Au-TiO2) heterostructures with different sizes of Au nanoparticles (NPs). Our study clearly demonstrates the essential role played by Au NP size in plasmon-driven H2O reduction and reveals two distinct mechanisms to clarify visible-light photocatalytic activity under different excitation conditions. The size of the Au NP governs the efficiency of plasmon-mediated electron transfer and plays a critical role in determining the reduction potentials of the electrons transferred to the TiO2 conduction band. Our discovery provides a facile method of manipulating photocatalytic activity simply by varying the Au NP size and is expected to greatly facilitate the design of suitable plasmonic photocatalysts for solar-to-fuel energy conversion.

We investigated changes in the Pt-Pt bond distance, particle size, crystallinity, and coordination of Pt nanoparticles as a function of particle size (1-3 nm) and adsorbate (H2, CO) using synchrotron radiation pair distribution function (PDF) and X-ray absorption spectroscopy (XAS) measurements. The ∼1 nm Pt nanoparticles showed a Pt-Pt bond distance contraction of ∼1.4%. The adsorption of H2 and CO at room temperature relaxed the Pt-Pt bond distance contraction to a value close to that of bulk fcc Pt. The adsorption of H2 improved the crystallinity of the small Pt nanoparticles. However, CO adsorption generated a more disordered fcc structure for the 1-3 nm Pt nanoparticles compared to the H2 adsorption Pt nanoparticles. In situ XANES measurements revealed that this disorder results from the electron back-donation of the Pt nanoparticles to CO, leading to a higher degree of rehybridization of the metal orbitals in the Pt-adsorbate system.

We report a facile, seed-mediated method to synthesize nanoscale gold truncated ditetragonal nanoprisms (TDPs) enclosed by 12 high-index {310} facets. The method leads to the formation of nanoparticles with high size and shape monodispersity and allows for easy surfactant removal. The dependence of particle shape on the synergetic contribution of metallic ions, halide ions, and surfactant adsorbates during synthesis is described. The resulting high-index nanoparticle facets were demonstrated as efficient activators of a supported catalytic material (platinum). A Pt monolayer deposited onto the Au TDP nanofacets with sharp electrochemical signatures exhibits an enhanced catalytic activity.

Au/TiO(2) catalysts used in the water-gas shift (WGS) reaction at 120 °C, 7% CO, 22% H(2)O, 9% CO(2), and 37% H(2) had rates up to 0.1 moles of CO converted per mole of Au per second. However, the rate per mole of Au depends strongly on the Au particle size. The use of a nonporous, model support allowed for imaging of the active catalyst and a precise determination of the gold size distribution using transmission electron microscopy (TEM) because all the gold is exposed on the surface. A physical model of Au/TiO(2) is used to show that corner atoms with fewer than seven neighboring gold atoms are the dominant active sites. The number of corner sites does not vary as particle size increases above 1 nm, giving the surprising result that the rate per gold cluster is independent of size.

We show that the noncrystalline-to-crystalline transition of supported Pt nanoparticles (NPs) in the subnanometer to nanometer size range is statistical in nature, and strongly affected by particle size, support, and adsorbates (here we use H2). Unlike in the bulk, a noncrystalline phase exists and is stable in small NPs, reflecting a general mesoscopic feature. Observations of >3000 particles by high-resolution transmission electron microscopy show a noncrystalline-to-crystalline transition zone that is nonabrupt; there is a size regime where disordered and ordered NPs coexist. The NP size at which this transition occurs is strongly dependent on both the adsorbate and the support, and this effect is general for late 5d transition metals. All results are reconciled via a statistical description of particle-support-adsorbate interactions.

Well-defined surfaces of Pt have been extensively studied for various catalytic processes. However, industrial catalysts are mostly composed of fine particles (e.g., nanocrystals), due to the desire for a high surface to volume ratio. Therefore, it is very important to explore and understand the catalytic processes both at nanoscale and on extended surfaces. In this report, a general synthetic method is described to prepare Pt nanocrystals with various morphologies. The synthesized Pt nanocrystals are further purified by exploiting the "self-cleaning" effect which results from the "colloidal recrystallization" of Pt supercrystals. The resulting high-purity nanocrystals enable the direct comparison of the reactivity of the {111} and {100} facets for important catalytic reactions. With these high-purity Pt nanocrystals, we have made several observations: Pt octahedra show higher poisoning tolerance in the electrooxidation of formic acid than Pt cubes; the oxidation of CO on Pt nanocrystals is structure insensitive when the partial pressure ratio p(O2)/p(CO) is close to or less than 0.5, while it is structure sensitive in the O(2)-rich environment; Pt octahedra have a lower activation energy than Pt cubes when catalyzing the electron transfer reaction between hexacyanoferrate (III) and thiosulfate ions. Through electrocatalysis, gas-phase-catalysis of CO oxidation, and a liquid-phase-catalysis of electron transfer reaction, we demonstrate that high quality Pt nanocrystals which have {111} and {100} facets selectively expose are ideal model materials to study catalysis at nanoscale.

Well-defined surface, such as surface of a single crystal, is being used to provide precise interpretation of catalytic processes, while the nanoparticulate model catalyst more closely represents the real catalysts that are used in industrial processes. Nanocrystal superlattice, which combines the chemical and physical properties of different materials in a single crystalline structure, is an ideal model catalyst, that bridge between conventional models and real catalysts. We identify the active sites for carbon monoxide (CO) oxidation on Au-FeO(x) catalysts by using Au-FeO(x) binary superlattices correlating the activity to the number density of catalytic contacts between Au and FeO(x). Moreover, using nanocrystal superlattices, we propose a general strategy of keeping active metals spatially confined to enhance the stability of metal catalysts. With a great range of nanocrystal superlattice structures and compositions, we establish that nanocrystal superlattices are useful model materials through which to explore, understand, and improve catalytic processes bridging the gap between traditional single crystal and supported catalyst studies.

Earth abundant copper-zinc-tin-chalcogenide (CZTSSe) is an important class of material for the development of low cost and sustainable thin film solar cells. The fabrication of CZTSSe solar cells by selenization of CZTS nanocrystals is presented. By tuning the composition of the CZTS nanocrystals and developing a robust film coating method, a total area efficiency as high as 7.2% under AM 1.5 illumination and light soaking has been achieved.