Hierarchical porous ceramic catalyst carriers, which exhibit good catalytic performance, are widely used in the petrochemical industry. However, the fabrication of ceramic carriers with hierarchically porous structures is highly challenging for conventional preparation processes. Thus, a strategy for designing and manufacturing hierarchically porous alumina ceramic catalyst carriers using aluminium trihydrate as raw material and powder bed fusion (PBF) as the forming process is proposed herein. PBF process parameters were optimised to define the processing window for creating ceramics with complex structures. Controllable pore characteristics in nano- and microscales has been achieved by combining dehydroxylation, PBF, and post-sintering processes. The effects of raw material composition and process parameters on crush strength, porosity, and specific surface area were systematically investigated. The resulting porous ceramics exhibit a crush strength of 86.03 ± 18.10 N/cm, specific surface area of 1.958 ± 0.123 m2/g, and porosity of 64.85 ± 1.15% with a multipeak distribution at 95 ± 1.23 nm and 17.76 ± 0.14 μm. The possibility of complicated monolithic catalyst carrier structures with bionic leaf vein characters has been validated for potential industrial applications. [ABSTRACT FROM AUTHOR]

Abstract: The effects of laser sintering parameters (laser power, scan speed and hatching space) and post sintering process (heating rate, sintering temperature and holding time) on the physical and mechanical properties of porcelain components have been investigated. The study has been carried out using the Taguchi''s method for the experimental design. In the laser sintering process, lower laser energy density and higher hatching space will increase the final mechanical properties of the porcelain components. A stress relief principle has been put forward to explain the different influence of the factors. The appropriate laser sintering parameters are attained in this paper: laser power 50W; scan speed 85mm/s; and hatching space 0.6mm. Sintering temperature has been determined to be the most important factor in the post sintering process. Appropriate sintering temperature for the laser sintered porcelain bodies is in the range of 1425–1475°C regarding the mechanical properties of the porcelain components. The maximum bending strength, 34.0±4.9MPa, is reached. [Copyright &y& Elsevier]