Search

Objectives The aim of this work was to evaluate the biomechanical behavior of one-piece zirconia implants with a functionally graded bioglass (BG) layer as compared to monolithic zirconia and BG-coated implants, using the finite element method (FEM). Methods Zirconia disks were infiltrated with bioglass S53P4 and then morphologically inspected by scanning electron microscopy (SEM) followed by mechanical analyses on micro-indentation tests for further biomechanical validation using the finite element method (FEM). On modeling, zirconia dental implants anchored into mandibular bone were simulated on occlusal loading as recorded under mastication. Three types of implants were simulated: i) free of BG coating, ii) with 100 μm or 150 μm thick conventional BG coatings; and iii) with graded BG coatings involving 3 different chemical composition distributions. The stress state at both implant and bone were evaluated using the FEM. The mechanically-induced bone remodelling was analyzed through the bone strain results. Results Infiltration of BG into a zirconia structure resulted in a ∼100 μm thick layer with an exponential-like gradation of chemical composition and properties. Regarding the FEM calculations, the BG coating induced up to 30% decrease on stress in the implant body when compared to the monolithic zirconia implant. The gradient of chemical composition also improved the stresses’ distribution. The stresses distribution towards the BG-coatings were significantly high and could lead to failure. Stresses on the bone were recorded down to its strength threshold, with insignificant influence of the coating layer. The bone strain values on all models indicates further bone remodelling although BG-coated and BG-graded zirconia implants showed the highest strain magnitude that may enhance the mechanical stimulation for bone maintenance. Significance Graded BG-zirconia dental implants showed enhanced overall biomechanical behaviour as compared to the BG-coated or monolithic zirconia dental implants. Also, such biomechanical improvements noticed for the BG-graded system should be considered in combination with the well-known osseointegration benefits of bioactive glasses.

Objectives The aim of this study was to evaluate the influence of a surface conditioning technique using laser ablation and acid etching on PEEK substrate on its bonding strength to a resin cement. Materials and methods Cylindrical specimens of unfilled PEEK, 30% glass fiber reinforced PEEK and 30% carbon fiber reinforced PEEK were separated in four groups according to the following surface treatments: acid etching with H2SO4, laser ablation with 200 µm holes spaced 400 µm apart (D2E4), laser ablation with 200 µm holes spaced 600 µm apart (D2E6), and laser ablation (D2E4) followed by acid etching. A dual-curing resin cement (Allcem CORE) was then applied to the PEEK surface. Specimens were aged in distilled water at 37 °C for 24 h. Shear bond strength tests were performed to the fracture of the samples. Two-way ANOVA statistical analysis was performed with a significance level of 0.05. Scanning electron microscopy analysis was performed to analyse the conditioned and fracture surfaces. Results SEM images of the test interfaces showed that the resin cement could not flow in the holes designed by the laser ablation on the PEEK surface. The shear bond strength of PEEK to resin cement was not improved by the surface modification of the PEEK. Also, there was a statistically significant decrease in shear bond strength for unfilled PEEK specimens. On carbon or glass reinforced PEEK, the change was not significant. SEM images of the fracture surfaces revealed that the failure mode was mainly adhesive. Conclusions Although laser ablation promoted the PEEK surface modification by the formation of retentive holes, the test resin cement could not thoroughly flow on the rough modified surfaces to establish an effective mechanical interlocking. That negatively affected the shear bonding strength of PEEK to the resin cement. Further studies should be carried out to increase the bonding between PEEK and resin cements.

Objectives The aim of this study was to evaluate the effect of laser surface structuring on the bond strength of feldspar-based porcelain to zirconia, as compared to conventional sandblasting treatment. Materials and methods Thirty cylindrical zirconia substrates, previously sintered, were divided in three groups according to the type of surface conditioning: 1) sandblasting with 50 µm Al2O3; 2) laser structuring (O25 µm holes); and 3) laser structuring (O50 µm holes). Porcelain was injected onto the zirconia substrates. X-ray diffractometry (XRD) was used to evaluate the influence of the laser treatment on zirconia crystallographic phases. Shear bond strength test was performed. Micrographs using SEM were used to evaluate the zirconia surface after each surface treatment and to evaluate the fracture surface after the shear test. Results The laser-structured groups presented the highest shear bond strength (65 ± 16 MPa and 65 ± 11 MPa, for the 25 µm and 50 µm holes, respectively). The sandblasting samples presented shear bond strength of 37 ± 16 MPa. XRD analysis showed that there was no phase transformation on the thermally affected surface due to laser action. Microcracks were created at some holes due to the high temperature gradient generated by laser. Significance Laser structuring significantly increased (up to 75%) the shear bond strength of zirconia to veneering porcelain as compared to conventional sandblasting treatment. Therefore, laser structuring arises as a surface conditioning method for producing stronger and long lasting zirconia-porcelain interfaces.