The present study aims to investigate the moisture absorption of polypropylene (PP)/rubberwood flour (RWF) composites and its effects on dimensional stability. The compositions included different grades of plastic, and the amounts of wood flour, maleic anhydride-grafted polypropylene (MAPP), and ultraviolet (UV) stabilizer were varied. The composite materials were manufactured into panels by a twin-screw extruder. Long-term water absorption (WA), long-term thickness swelling (TS), and degradation of flexural properties of the composites were studied for a range of water immersion times. The WA and TS of the samples increased with RWF content and immersion time. Recycled PP gave higher WA and TS than virgin PP, for the composites with 45 wt% RWF. Increasing MAPP content from 3 to 5 wt% had no significant effect on WA and TS, whereas the addition of 1 wt% UV stabilizer increased them. A MAPP content of 3 wt% is recommended for moisture resistance, while the amount of UV stabilizer should be kept as low as possible. Flexural strength and modulus of composites also decreased with moisture uptake; however, <3% WA did not significantly affect the flexural strength. In contrast, the maximum strain of composites consistently increased with WA. [ABSTRACT FROM AUTHOR]

The mechanical properties of composites from recycled waste plastic and waste sawdust are of interest in trying to convert these waste streams to useful products. The development of these composites from natural fiber is therefore receiving widespread attention due to the growing environmental awareness. The effects of compositions were investigated including different grades of plastic (virgin and recycled) and amounts of wood flour, coupling agent, and ultraviolet (UV) stabilizer on mechanical and physical properties of polypropylene/rubberwood flour (RWF) composites. Virgin polypropylene gave better mechanical properties than recycled (recycled polypropylene (rPP)), both in composites and as unfilled plastic. RWF content exceeding 25 wt% enhanced the strength of RWF-reinforced rPP composites. The modulus and hardness of composites increased linearly with wood flour loadings. Maleic anhydride-grafted polypropylene (MAPP) as a coupling agent increased the strength, modulus, and hardness of the composites. However, addition of 1 wt% UV stabilizer degraded the mechanical properties. Therefore, 4 wt% MAPP content is recommended to achieve good mechanical properties of rPP/RWF composites, while the amount of UV stabilizer should be as small as possible to avoid its negative influence. [ABSTRACT FROM AUTHOR]