We report the effect of topographical features on gold nanowire assemblies in a vertically applied AC electric field. Nanowires 300 nm in diameter ×2.5 μm long, and coated with ∼30 nm silica shell, were assembled in aqueous solution between top and bottom electrodes, where the bottom electrode was patterned with cylindrical dielectric posts. Assemblies were monitored in real time using optical microscopy. Dielectrophoretic and electrohydrodynamic forces were manipulated through frequency and voltage variation, organizing nanowires parallel to the field lines, i.e., standing perpendicular to the substrate surface. Field gradients around the posts were simulated and assembly behavior was experimentally evaluated as a function of patterned feature diameter and spacing. The electric field gradient was highest around these topographic features, which resulted in accumulation of vertically oriented nanowires around the post perimeters when dielectrophoresis dominated (high AC frequency) or between the posts when electrohydrodynamics dominated (low AC frequency). This general type of reconfigurable assembly, coupled with judicious choice of nanowire and post materials/dimensions, could ultimately enable new types of optical materials capable of switching between two functional states by changing the applied field conditions.

Ordered two-dimensional (2D) lattices were formed by assembling silica-coated solid and segmented Au nanowires between coplanar electrodes using alternating current (ac) electric fields. Dielectrophoretic forces from the ac field concentrated wires between the electrodes, with their long axis aligned parallel to the field lines. After reaching a sufficient particle density, field-induced dipolar interactions resulted in the assembly of dense 2D lattices that spanned the electrodes, a distance of at least ten wire lengths. The ends of neighboring Au wires or segments overlapped a fraction of their length to form lattice structures with a "running bond" brickwork-like pattern. The observed lattice structures were tunable in three distinct ways: (1) particle segmentation pattern, which fixed the lattice periodicity for a given field condition; (2) ac frequency, which varied lattice periodicity in real time; and (3) switching the field on/off, which converted between lattice and smectic particle organizations. Electric field simulations were performed to understand how the observed lattice periodicity depends on the assembly conditions and particle segmentation. Directed self-assembly of well-ordered 2D metallic nanowire lattices that can be designed by Au striping pattern and reconfigured by changes in field conditions could enable new types of switchable optical or electronic devices.