To study polymer-dispersed liquid crystal (PDLC) films doped with indium tin oxide (ITO) nanoparticles (NPs), samples were prepared by ultraviolet-initiated polymerisation based on the thiol-acrylate system. Owing to the interaction between PDLC system and ITO NPs, the content and the size of ITO NPs are the main determinants to the microstructure which plays an essential role on the electro-optical and anti-infrared properties of the PDLC films. In the polymer matrix, a novel microstructure consisting of a dense surface, micron-sized meshes and submicron meshes is found to benefit the better performances of the low driven voltage (20.7 V), the relatively high contrast ratio (8.3) and the lowest transmittance(500-2500 nm) on average at about 3.55% with maximum of merely 7.6%. Thus, it lays a solid foundation for the further investigations on the microstructure and the performance of the PDLC films. Meanwhile, it is proved that the PDLC film, improved performance through doping ITO NPs, is promising to be a superior choice in the field of energy-saving. [ABSTRACT FROM AUTHOR]

To study effects of the crosslinking agent/diluents/thiol on morphology of the polymer matrix and the electro-optical properties of polymer-dispersed liquid crystal (PDLC) films, samples were prepared by ultraviolet (UV)-initiated polymerisation. Due to the interaction between thiol-acrylate reaction and acrylate monomers polymerisation, the sample compositions were the foremost determinant to the microstructures which in turn played an essential role on the electro-optical properties of the PDLC films. With the increasing content of the crosslinking agent, the LC droplet size decreased, while the thiol had a contrary effect on the LC droplet size. It was demonstrated that the superior properties of the low-driven voltage (37.2 V), the high contrast ratio (148.2), the short response time (14.9 ms) and the high saturation transmittance (86.6%) could benefit from a novel microstructure which had a dense surface and meshes with microspheres attached. It was of great significance for the optimisation and the potential applications of the PDLC films. [ABSTRACT FROM AUTHOR]