Search

Chemical shrinkage (CS) is an intrinsic parameter that may affect the early age cracking of paste, mortar and concrete. It is well known as the driving force of self-desiccation, autogenous shrinkage (AGS) and drying shrinkage. During the first stage of cement hydration (at the initial setting time), the CS and AGS are equal. In the hardened stages, there is a difference in values between the two shrinkage parameters. This paper is a comprehensive review on CS and AGS, measurement techniques, modeling and prediction of different cementitious systems. Based on the various experimental studies, chemical shrinkage depends on the water to binder ratio (w/b) and is proportional to the degree of hydration. A low w/b ratio leads to high CS and AGS. The composition of cement has an effect on both CS and AGS. Also, incorporating supplementary cementitious materials (SCMs) affects both shrinkage parameters. It is concluded that adding fly ash (FA) to concrete contributes to CS and AGS reductions. However, this is not the case when concrete contains slag. More than 170 references were consulted including 35 which were published after 2020. According to the authors knowledge, there is no published work on the effect of fibers, especially bio-fibers, on the chemical shrinkage of cement-based composites. Therefore, in addition to traditional chemical shrinkage of cementitious systems, this review includes a section on recent papers conducted by the authors on the effect of bio-fibers on the chemical shrinkage of cement composites. [ABSTRACT FROM AUTHOR]

Using limestone powder (LP), the by-product of manufactured sand, to replace part of fly ash (FA) or manufactured sand could not only turn waste into treasure and decrease the price of concrete, but could also enhance the performance of concrete and reduce environmental pollution. However, the impact of various LP incorporation methods on the performance of mass concrete was inconsistent. In this paper, the effects of LP on the workability, compressive strength, constrained expansion rate, hydration temperature and impermeability of mass concrete were studied by replacing FA or manufactured sand alone and replacing FA and manufactured sand simultaneously. The results showed that the impact of LP on the performance of mass concrete was equal when it replaced FA alone and FA and manufactured sand at the same time. When the replacement amount was 20%, the workability, expansibility and early strength of concrete were improved, but the later strength and impermeability were slightly reduced. The workability, compressive strength, expansibility and impermeability of mass concrete were improved when manufactured sand was replaced alone, and the optimal dosage was 10%. The LP, moreover, reduced the hydration temperature peak of concrete in three kinds of mixing methods, but the temperature peak appeared earlier. At lower dosages, LP optimized pore structure and promoted the early hydration of cement through filler effects and nucleation effects. When LP replaced manufactured sand, the microstructure of concrete was more dense, so the replacement of manufactured sand had a better effect on the improvement of concrete properties. A reference value for the use of LP in mass concrete is provided in this study. [ABSTRACT FROM AUTHOR]

Recycling of multi-source solid waste is of great benefit to energy conservation and environmental governance. In this paper, a new type of environmental protection concrete for railway accessory facilities was prepared from silicon-manganese slag, steel slag, fly ash and recycled macadam. Seven kinds of concrete with different mix proportions were designed. Through unconfined compressive strength, splitting, drying shrinkage and temperature shrinkage tests, the multivariate changing trends of steel slag content, cement dosage and age on the anti-interference ability of concrete were investigated. The main mechanisms of the development of mechanical and dry shrinkage properties were revealed by the hydration process of 3SR-60. The results show that 3SR-60 had better mechanical strength under the same cement dosage. The temperature shrinkage strain decreased and then increased with the rise of the proportion of waste residue, increased with the addition of cement dosage and decreased first and then increased with the descent in the temperature. The temperature shrinkage coefficient reached the lowest value at 0–10 °C. The drying shrinkage coefficient decreases with the increase in the proportion of waste residue and increases with the increase in cement dosage. The dry shrinkage strain increased rapidly during the first 8 days and became almost constant after 30 days. Cementation of calcium silicate hydrate (C-S-H) and ettringite (AFt) developed continuously and filled the internal pores of the structure, interlocking and cementing with each other, which made the microstructure develop from a three-dimensional network to a dense complex, and the macro dimension was reflected in the enhancement of the power to resist external interference. The conclusion of the test summarized that SR-60 had preferable mechanical and shrinkage performance. [ABSTRACT FROM AUTHOR]