Search

In this paper, the workability, mechanical, ion leaching, and drying shrinkage properties of alkali-activated concrete with recycled coarse and fine aggregates were studied, and the pore structure and micro-morphology of different alkali-activated recycled aggregate concretes (AARACs) were characterized by using the mercury intrusion method and scanning electron microscopy, respectively. The experimental results showed that with the increase in the replacement rate of the recycled fine aggregate (RFA), the flowability showed a decreasing trend. Adding a certain amount of RFA improves the mechanical properties of the AARAC. The compressive strength at a curing age of 28 days was 65.3 MPa with 70 wt% RFA replacement. When the replacement rate of the RFA was 100 wt%, the maximum splitting tensile strength (4.5 MPa) was obtained at a curing age of 7 days. However, the addition of the RFA had little effect on the flexural strength of the AARAC. As an extension of the curing age, the splitting tensile strength, flexural strength, tension-to-compression ratio, and flexure-to-compression ratio all showed an increasing trend at first and then a decreasing trend. At a curing age of 7 days, the tension-to-compression ratio and flexure-to-compression ratio were both high (except for those of R100), indicating that the ductility and toughness of the specimen were improved. The addition of the RFA increased the drying shrinkage of the AARAC. At a curing age of 120 days, compared to the specimen without the RFA, the drying shrinkage rate of the specimen with the addition of 70 wt% RFA increased by 34.15%. As the curing age increased, the microstructure of the reaction products became denser, but the proportion of large-diameter pores increased. This study evaluated the application of RFA in AARAC. The experimental results showed that the RFA-based AARAC had acceptable mechanical and durability properties. [ABSTRACT FROM AUTHOR]

Recycling of multi-source solid waste is of great benefit to energy conservation and environmental governance. In this paper, a new type of environmental protection concrete for railway accessory facilities was prepared from silicon-manganese slag, steel slag, fly ash and recycled macadam. Seven kinds of concrete with different mix proportions were designed. Through unconfined compressive strength, splitting, drying shrinkage and temperature shrinkage tests, the multivariate changing trends of steel slag content, cement dosage and age on the anti-interference ability of concrete were investigated. The main mechanisms of the development of mechanical and dry shrinkage properties were revealed by the hydration process of 3SR-60. The results show that 3SR-60 had better mechanical strength under the same cement dosage. The temperature shrinkage strain decreased and then increased with the rise of the proportion of waste residue, increased with the addition of cement dosage and decreased first and then increased with the descent in the temperature. The temperature shrinkage coefficient reached the lowest value at 0–10 °C. The drying shrinkage coefficient decreases with the increase in the proportion of waste residue and increases with the increase in cement dosage. The dry shrinkage strain increased rapidly during the first 8 days and became almost constant after 30 days. Cementation of calcium silicate hydrate (C-S-H) and ettringite (AFt) developed continuously and filled the internal pores of the structure, interlocking and cementing with each other, which made the microstructure develop from a three-dimensional network to a dense complex, and the macro dimension was reflected in the enhancement of the power to resist external interference. The conclusion of the test summarized that SR-60 had preferable mechanical and shrinkage performance. [ABSTRACT FROM AUTHOR]