Search

The axial compressive behaviours of coal gangue concrete-filled steel tube (GCFST) columns after chloride salt corrosion were investigated numerically. Numerical modelling was conducted through the static analysis method by finite element (FE) analysis. The failure mechanism, residual strength, and axial load–displacement curves were validated against tests of the coal gangue aggregate concrete-filled steel tube (GCFST) columns at room and natural aggregate concrete-filled steel tube (NCFST) columns after salt corrosion circumstance. According to the analysis on the stress distribution of the steel tube, the stress value of the steel tube decreased as the corrosion rate increased at the same characteristic point. A parametric analysis was carried out to determine the effect of crucial variation on residual strength. It indicated that material strength, the steel ratio, and the corrosion rate made a profound impact on the residual strength from the FE. The residual strength of the columns exposed to chloride salt was in negative correlation with the corrosion rate. The impact on the residual strength of the column was little, obvious by the replacement rate of the coal gangue. A simplified design formula for predicting the ultimate strength of GCFST columns after chloride salt corrosion exposure was proposed. [ABSTRACT FROM AUTHOR]

Graphene has attracted much interest in many scientific fields because of its high specific surface area, Young's modulus, fracture strength, carrier mobility and thermal conductivity. In particular, the graphene oxide (GO) prepared by chemical exfoliation of graphite has achieved low-cost and large-scale production and is one of the most promising for Cu matrix composites. Here, we prepared a high strength, high electrical conductivity and high thermal conductivity reduced graphene oxide (RGO)/Cu composite by directly heating the GO/copper formate. The oxygen-containing functional groups and defects of RGO are significantly reduced compared with those of GO. The tensile yield strength and thermal conductivity of RGO/Cu composite with RGO volume fraction of 0.49 vol.% are as high as 553 MPa and 364 W/(m·K) at room temperature, respectively. The theoretical value of the tensile yield strength of the composite is calculated according to the strengthening mechanism, and the result shows that it agrees with the experimental value. After hot-rolling treatment, the ductility and conductivity of the composite materials have been greatly improved, and the ductility of the RGO/Cu composite with RGO volume fraction of 0.49 vol.% has been increased to four times the original. This work provides a highly efficient way to fabricate a high-performance RGO-reinforced Cu composite for commercial application. [ABSTRACT FROM AUTHOR]

Dielectric elastomers (DEs) are a class of electro-active polymers (EAPs) that can deform under electric stimuli and have great application potential in bionic robots, biomedical devices, energy harvesters, and many other areas due to their outstanding deformation abilities. It has been found that stretching rate, temperature, and electric field have significant effects on the stress-strain relations of DEs, which may result in the failure of DEs in their applications. Thus, this paper aims to develop a thermo-electro-viscoelastic model for DEs at finite deformation and simulate the highly nonlinear stress-strain relations of DEs under various thermo-electro-mechanical loading conditions. To do so, a thermodynamically consistent continuum theoretical framework is developed for thermo-electro-mechanically coupling problems, and then specific constitutive equations are given to describe the thermo-electro-viscoelastic behaviors of DEs. Furthermore, the present model is fitted with the experimental data of VHB4905 to determine a temperature-dependent function of the equilibrium modulus. A comparison of the nonlinear loading-unloading curves between the model prediction and the experimental data of VHB4905 at various thermo-electro-mechanical loading conditions verifies the present model and shows its ability to simulate the thermo-electro-viscoelastic behaviors of DEs. Simultaneously, the results reveal the softening phenomena and the instant pre-stretch induced by temperature and the electric field, respectively. This work is conducive to analyzing the failure of DEs in functionalities and structures from theoretical aspects at various thermo-electro-mechanical conditions. [ABSTRACT FROM AUTHOR]

In order to study the variation of mechanical properties of steel under acid rain corrosion conditions in northern China, monotonic tensile tests were conducted on Q235 steel with a thickness of 3.0 mm and 4.5 mm using a method of artificially prepared simulated acid rain solution for indoor accelerated corrosion. The results show that the failure mode of corroded steel standard tensile coupon includes normal fault and oblique fault. The failure patterns of the test specimen show that the thickness of the steel and corrosion rate affected the corrosion resistance. Larger thicknesses and lower corrosion rates will delay the failure mode of corrosion on steel. The strength reduction factor (Ru), deformability reduction factor (Rd) and energy absorption reduction factor (Re) decrease linearly with the increasing corrosion rate from 0% to 30%. The results are interpreted also from the microstructural point of view. The number, size, and distribution of the pits are random when the steel is subjected to sulfate corrosion. The higher the corrosion rate, the clearer, denser, and more hemispherical the corrosion pits. The microstructure of steel tensile fracture can be divided into intergranular fracture and cleavage fracture. As the corrosion rate increases, the dimples at the tensile fracture gradually disappear and the cleavage surface gradually increases. An equivalent thickness reduction model is proposed based on Faraday's law and the meso-damage theory. [ABSTRACT FROM AUTHOR]

The hysteretic behavior of square concrete-filled steel tube (CFST) stub columns subjected to sulfate corrosion and freeze-thaw cycle is examined by numerical investigation. The constitutive model of steel considered the Bauschinger effect, and compression (tension) damage coefficient was also adopted for the constitutive model of core concrete. The experimental results are used to verify the finite element (FE) model, which could accurately predict the hysteretic behaviors of the CFST piers. Then, the effects of the yield strength of steel, compressive strength of concrete, steel ratio, axial compression ratio, and alternation time on ultimate horizontal load are evaluated by a parametric study. The results showed that the yield strength of steel and the steel ratio have a positive effect of hysteretic behavior. The compressive strength of concrete and alternation time significantly decreased the unloading stiffness which causes the pinching phenomenon. The yield strength of steel, compressive strength of concrete, and alternation time of environmental factors (corrosion-freeze-thaw cycles) has no obvious effect on the initial stiffness, while the steel ratio has a remarkable effect. The ultimate horizontal load increases with the increasing steel ratio, yield strength of steel and compressive strength of concrete. Meanwhile, the decrement of alternation time led to the increase of ultimate horizontal load. This suggests that the confinement coefficient and alternation time are the two main factors that impact the ultimate horizontal load. A formula which considers the reduction coefficient for the ultimate horizontal load of the CFST columns subjected to sulfate corrosion and freeze-thaw cycles is proposed. The formulae can accurately predict the ultimate horizontal load with mean value of 1.022 and standard deviation of 0.003. [ABSTRACT FROM AUTHOR]

Zirconium oxide (ZrO2) is widely used as the thermal barrier coating in turbines and engines. Accurate emissivity measurement of ZrO2 coating at high temperatures, especially above 1000 °C, plays a vital role in thermal modelling and radiation thermometry. However, it is an extremely challenging enterprise, and very few high temperature emissivity results with rigorously estimated uncertainties have been published to date. The key issue for accurately measuring the high temperature emissivity is maintaining a hot surface without reflection from the hot environment, and avoiding passive or active oxidation of material, which will modify the emissivity. In this paper, a novel modified integrated blackbody method is reported to measure the high temperature normal spectral emissivity of ZrO2 coating in the temperature range 1000 °C to 1200 °C and spectral range 8 μm to 14 μm. The results and the associated uncertainty of the measurement were estimated and a relative standard uncertainty better than 7% (k = 2) is achieved. [ABSTRACT FROM AUTHOR]

Low tensile strength, poor elastic modulus, and complex concrete cracking work condition are almost unavoidable due to the intrinsic brittleness. To deal with concrete maintenance and durability, microbial self-healing concretes have been rapidly developed and widely applied recently. The microbial self-healing can specifically patch fractures as well as boost the concrete structure's capacity, durability, and permeability. This paper presents the state-of-the-art in the microbe induced self-healing in cement-based composites. The microorganism and carriers were classified according to the working theory and repair effects. Additionally, the precise efficiency and effect of various technologies are also evaluated for microbial immobilization. Based on the literature review and summary from the perspective of microorganism, carriers, and immobilization methods, challenges and further works are discussed. [ABSTRACT FROM AUTHOR]