Search

In this work, squeeze casting experiments of flywheel housing components with a large wall thickness difference and a complex shape were carried out with AlSi9Mg aluminum alloy. The defects, microstructures, and mechanical properties under different process parameters were investigated. Furthermore, the local pressurization process was applied to the thick-walled positions to force-feed the cast defects. The mechanical properties and microstructures at these positions were analyzed. The results showed that the surface quality of formed components was good and that local pressurization could effectively reduce the shrinkage cavity and shrinkage porosity in thick walls, but the scope and effect of forced feeding were limited. The optimum process parameters were a pouring temperature of 650 °C, a specific pressure of 48 MPa, a mold temperature of 220 °C, a local pressurization of 800 MPa, and pressure delay times of 15 s (side A) and 17 s (side B). The ultimate tensile strength, yield strength, and elongation of the formed component under validation experiments of the optimum process parameters were 201 MPa, 103 MPa, and 5.1%. Meanwhile, the fine grains of primary α-Al were mainly rosette and equiaxed grains, and the average grain size was about 40 μm. The microstructure of the eutectic silicon was acicular and was prone to segregation under pressure. According to profile morphology, the positions after pressurization were divided into a deformation zone, a direct action zone, and an indirect action zone. The coexistence of as-cast and plastic deformation microstructures was observed. The effect of local pressurization mainly involved a change in the solidification process, plastic deformation, and forced feeding. [ABSTRACT FROM AUTHOR]

This study aimed to investigate the impact of corrosion on the microstructure and tensile properties of 7075 high-strength alloy. It involved outdoor exposure tests in an actual marine atmospheric environment in Wanning, Hainan Province. The results showed that the 7075 alloy was corroded rapidly in the marine atmospheric environment, and corrosion pits and intergranular cracks were generated. The intergranular cracks were extended along the grain boundary during corrosion, leading to the exfoliation of the matrix. The cause for the intergranular corrosion was discussed based on the microstructure characteristics of 7075 alloy. The tensile properties of the 7075 alloy gradually deteriorated with the increase of exposure time in the marine atmospheric environment. The ultimate strength and elongation were decreased by about 3.2% and 58.3%, respectively, after 12 months of outdoor exposure. [ABSTRACT FROM AUTHOR]

The effect of recrystallization annealing on corrosion behavior of Ta-4%W alloy was studied. It is found that the deformed sample contains high dense dislocations and dislocation boundaries. During annealing, these dislocations and dislocation boundaries are replaced by recrystallizing grains until the alloy is fully recrystallized. Both the anodic dissolution and the cathodic activity is much more blocked. The corrosion potential gradual shift towards negative values and corrosion current density decrease, while polarization resistance increases after annealing, indicating enhanced corrosion resistance of the alloy. Such an enhancement is caused by the increase of low-Σ coincide site lattice boundaries and decrease of dislocations and dislocation boundaries. [ABSTRACT FROM AUTHOR]