A feasible approach was developed for the synthesis of ordered mesoporous SBA-15-type materials using coal fly ash (CFA) as raw material. In the proposed approach, CFA was, firstly, activated by subcritical water with the addition of NaOH, which allowed an efficient extraction of silicon species from CFA under strong acidic conditions at near room temperature. Subsequently, in the synthesis system, using silicon extraction solution as the silicon precursor, the introduction of anhydrous ethanol as a co-solvent effectively inhibited the polymerization of silanol species and promoted their collaborative self-assembly with surfactant molecules by enhancing the hydrogen bond interactions. The resultant SBA-15 material had a high purity, high specific surface area (1014 m2/g) and pore volume (1.08 cm3/g), and a highly ordered mesostructure, and, therefore, exhibited an excellent removal efficiency (90.5%) and adsorption capacity (160.8 mg/g) for methylene blue (MB) from simulated wastewater. Additionally, the generation of surface acid sites from the homogenous incorporation of Al atoms onto the mesoporous walls of SBA-15 combined with the perfect retention of the ordered mesostructure endowed the obtained Al-SBA-15 material with a further boost in the removal performance of MB. The MB removal efficiency can reach ~100%, along with a maximum adsorption capacity of 190.1 mg/g. [ABSTRACT FROM AUTHOR]

Ordered mesoporous Zr-Al composite oxide materials (denoted as OMZA-x) with different Zr contents have been synthesized by a solvent evaporation-inducing self-assembly procedure associated with a thermal treatment at 100 °C. A cooperative co-assembly process of amphiphilic triblock copolymer F127 molecules and inorganic hydroxyl species originated from the hydrolysis of Zr and Al precursors was proposed to explain the synthesis of OMZA-x. Compared to ordered mesoporous alumina prepared without introducing Zr species, the resultant OMZA-x exhibited a much more ordered mesostructure combined with a distinct increase in the pore volume and specific surface area. The highly homogenous doping of Zr into the mesopore walls together with the formation of Zr-O-Al bonds can effectively enhance the thermal and hydrothermal stability of OMZA-x. For instance, the ordered mesostructure and excellent textural properties of OMZA-6 prepared with the optimum atomic ratio of Al to Zr of 6 could be well maintained even after a high-temperature treatment at 1000 °C for 1 h or a hydrothermal treatment at 100 °C for 6 h. [ABSTRACT FROM AUTHOR]