Search

In recent years, Zn and its alloys have become some of the most promising degradable metals as in vivo implants due to their acceptable biocompatibility and more suitable degradation rate compared with Mg-based and Fe-based alloys. However, the degradation rate of Zn-based materials after implantation in the body for orthopedic applications is relatively slow, leading to long-term retention of the implants after fulfilling their missions. Moreover, the excessive release of Zn2+ during the degradation process of Zn-based implants usually leads to high cytotoxicity and delayed osseointegration. To provide a feasible solution to the problem faced by Zn-based implants, a Zn-Ca composite was fabricated by an air pressure infiltration method in this work. The XRD pattern of the composite suggests that the composite is fully composed of Zn-Ca intermetallic compounds. The degradation tests in vitro show that the composite has a much higher degradation rate than pure Zn, and the high Ca content regions in the composite can preferentially degrade as sacrificial anodes. In addition, the composite can efficiently induce Ca-P deposition during immersion tests in Hank's solution. Cytotoxicity tests indicate that L-929 cells exhibit around 82% cell viability (Grade 1) even after being cultured in the 100% extract prepared from the Zn-Ca composite for 1 day and show excellent cell viability. [ABSTRACT FROM AUTHOR]

Aluminum and its alloys are widely used in packaging, transportation, electrical materials, and many other fields because of their abundance, light weight, good mechanical properties, suitable corrosion resistance, excellent electrical conductivity, and other advantages. Grain refinement achieved by adding inoculant is important not only to reduce the segregation and thermal cracking of alloy castings but also to improve the mechanical properties of alloy castings. Therefore, fine equiaxed grain structure has always been one of the goals pursued by the aluminum alloy casting industry. For this reason, the selection and development of effective inoculants for aluminum alloy is a key technology in the aluminum processing industry. This paper summarizes the development history of inoculants for aluminum alloy, including Al-Ti-C, Al-Ti-B, Al-Ti, Al-Ti-B-(C)-Ce, Al-Sc, and the Fe-rich phase of Al-Si alloy. At the same time, the advantages and disadvantages of common inoculants are introduced and prospective future applications are reviewed. [ABSTRACT FROM AUTHOR]

The mechanical properties of iron-rich Al–Si alloy is limited by the existence of plenty of the iron-rich phase (β-Al5FeSi), whose unfavorable morphology not only splits the matrix but also causes both stress concentration and interface mismatch with the Al matrix. The effect of the cooling rate on the tensile properties of Fe-rich Al–Si alloy was studied by the melt spinning method at different rotating speeds. At the traditional casting cooling rate of ~10 K/s, the size of the needle-like β-Al5FeSi phase is about 80 μm. In contrast, the size of the β-Al5FeSi phase is reduced to 500 nm and the morphology changes to a granular morphology with the high cooling rate of ~104 K/s. With the increase of the cooling rate, the morphology of the β-Al5FeSi phase is optimized, meanwhile the tensile properties of Fe-rich Al–Si alloy are greatly improved. The improved tensile properties of the Fe-rich Al-Si alloy is attributed to the combination of Fe-rich reinforced particles and the granular silicon phase provided by the high cooling rate of the melt spinning method. [ABSTRACT FROM AUTHOR]