This work reports on the fabrication of a novel two-layer material composed of a porous tantalum core and a dense Ti6Al4V (Ti64) shell by powder metallurgy. The porous core was obtained by mixing Ta particles and salt space-holders to create large pores, the green compact was obtained by pressing. The sintering behavior of the two-layer sample was studied by dilatometry. The interface bonding between the Ti64 and Ta layers was analyzed by SEM, and the pore characteristics were analyzed by computed microtomography. Images showed that two distinct layers were obtained with a bonding achieved by the solid-state diffusion of Ta particles into Ti64 during sintering. The formation of β-Ti and α′ martensitic phases confirmed the diffusion of Ta. The pore size distribution was in the size range of 80 to 500 µm, and a permeability value of 6 × 10−10 m2 was close to the trabecular bones one. The mechanical properties of the component were dominated mainly by the porous layer, and Young's modulus of 16 GPa was in the range of bones. Additionally, the density of this material (6 g/cm3) was much lower than the one of pure Ta, which helps to reduce the weight for the desired applications. These results indicate that structurally hybridized materials, also known as composites, with specific property profiles can improve the response to osseointegration for bone implant applications. [ABSTRACT FROM AUTHOR]

We present a novel Ti64/20Ag highly porous composite fabricated by powder metallurgy for biomedical applications and provide an insight into its microstructure and mechanical proprieties. In this work, the Ti64/20Ag highly porous composites were successfully fabricated by the space holder technique and consolidated by liquid phase sintering, at lower temperatures than the ones used for Ti64 materials. The sintering densification was evaluated by dilatometry tests and the microstructural characterization and porosity features were determined by scanning electron microscopy and computed microtomography. Permeability was estimated by numerical simulations on the 3D real microstructure. Mechanical properties were evaluated by simple compression tests. Densification was achieved by interparticle pore filling with liquid Ag that does not drain to the large pores, with additional densification due to the macroscopical deformation of large pores. Pore characteristics are closely linked to the pore formers and the permeability was highly increased by increasing the pore volume fraction, mainly because the connectivity was improved. As expected, with the increase in porosity, the mechanical properties decreased. These results permitted us to gain a greater understanding of the microstructure and to confirm that we developed a promising Ti64/20Ag composite, showing E of 7.4 GPa, σy of 123 MPa and permeability of 3.93 × 10−11 m2. Enhanced adaptability and antibacterial proprieties due to Ag were obtained for bone implant applications. [ABSTRACT FROM AUTHOR]