In order to apply the rigid biodegradable PLA material for flexible toothbrush bristle products, in this paper, Poly(lactic acid) (PLA) and thermoplastic polyurethane elastomer (TPU) blends (TPU/PLA composites), with a mass ratio of 80:20, were prepared by the melt-blending method to achieve toughening modification. Infrared spectroscopy, scanning electron microscopy, differential scanning calorimetry and low-field nuclear magnetic resonance were used to investigate the effect of the compatibilizer, Maleic anhydride grafted polypropylene (PP-g-MAH), on the compatibility of the blends, and the effect of melamine on the flame retardant properties of the blends was further investigated. The results demonstrated that 3% PP-g-MAH had the best compatibility effect on PLA and TPU; the TPU/PLA composites have a better macromolecular motility and higher crystallization capacity in the amorphous regions through the physical and chemical action by using PP-g-MAH as a compatibilizer. By adding melamine as a flame retardant, the scorch wire ignition temperature of TPU/PLA composites can reach 830 °C, which was elevated by 80 °C compared with pure PLA; however, the flame retardant effect of melamine in a single system was not significant. Melamine acts as a flame retardant by absorbing heat through decomposition and diluting the combustible material by producing an inert gas. [ABSTRACT FROM AUTHOR]

Mechanical properties of thermoplastic polyurethane elastomers based on either polyether or polycarbonate (PC)-glycols, 4,4'-dipheylmethane diisocyanate (1,1'-methylenebis(4-isocyanatobenzene)), 1,4-butanediol, were controlled by restriction of crystallization of polymer glycols. For the polyether glycol based-polyurethane elastomers (PUEs), poly(oxytetramethylene) glycol (PTMG), and PTMG incorporating dimethyl groups (PTG-X) and methyl side groups (PTG-L) were employed as a polymer glycol. For the PC-glycol, the randomly copolymerized PC-glycols with hexamethylene (C6) and tetramethylene (C4) units between carbonate groups with various composition ratios (C4/C6 = 0/100, 50/50, 70/30 and 90/10) were employed. The degree of microphase separation and mechanical properties of both the PUEs were investigated using differential scanning calorimetry, dynamic viscoelastic property measurements and tensile testing. Mechanical properties could be controlled by changing the molar ratio of two different monomer components. [ABSTRACT FROM AUTHOR]