Search

Top seal failure of ram blowout preventer (BOP) is one of the main factors leading to well control risk. The constitutive model and parameters of nitrile butadiene rubber (NBR) were optimized by compression and tensile tests, and the failure analysis model of the contact seal of the ram BOP top seal was built. The nonlinear contact mechanical behavior of the connection part of the BOP top seal was analyzed by the finite element method. Then, the influence of corrosion and wear defects at the top seal position of the 2FZ35-70 BOP under rated working pressure on the contact seal were studied, and the results showed that the overall contact pressure distribution of the top seal corrosion defects was uniform, the local contact pressure of the corrosion pit edge increased, and the top contact pressure decreased. The overall contact pressure of the wear defect of the top seal decreased linearly, the contact pressure at the maximum depth of the wear defect was the smallest, and the contact pressure gradually decreased to both sides. Ultimately, to guarantee the safety and reliability of the ram BOP, it is suggested that the acceptable depths of the seal corrosion pit and the wear at the top of the ram BOP are 4.0 mm and 0.2 mm, respectively, thus the reliability evaluation problem of the quantitative seal of the ram BOP top seal is solved. [ABSTRACT FROM AUTHOR]

Magnetized soft ferromagnetic films with micrometer thickness were studied. A FeSi film, with a total thickness of 2000 nm, separated by 10 nm-thick Ta interlayers, was fabricated using the direct-current magnetron sputtering technique. The thickness of each FeSi layer between adjacent Ta layers was 100 nm. Hysteresis loop measurement was used to characterize the magnetic properties of the layer. X-ray diffraction patterns and high-resolution transmission electron microscopy were used to characterize its texture. The experimental results showed that the FeSi film separated by Ta interlayers exhibited a lower saturation magnetization and a higher coercivity than those of the 1140 nm-thick FeSi film. The insertion of Ta interlayers resulted in the disappearance of the crystal plane of FeSi (221), and better texture of the crystal plane of FeSi (210). The FeSi film exhibited a crystal plane of FeSi (210) with a bcc crystalline structure. The Ta interlayers were partially amorphous, exhibiting crystal plane of Ta (002) and TaSi2 (310). The matching of magnetic properties between interlayers and soft magnetic layers played an important role in maintaining its soft magnetic properties. [ABSTRACT FROM AUTHOR]

This study aims to investigate an accurate detection method to detect defects in the gasket ring groove of the blowout preventer (BOP) using the ultrasonic phased array technology. Traditionally, it is difficult to accurately determine the type and size of defects in the gasket ring groove due to the complexity of the BOP configuration and the interference between the defect echo and the structural echo when using the ultrasonic phased array detection technology. In this study, firstly, the appropriate detection process parameters are determined by using simulation software for simulating and analyzing the defects of different sizes and types in the gasket ring groove of a BOP. Thereafter, according to the detection process parameters determined by the simulation analysis, we carry out a corresponding actual detection test. Simulation analysis and detection test results show that the relative amplitude of the test results and the simulation results differ within 1 dB, and the simulation results have a guiding role for the actual detection. The defect echo and structure echo can be clearly distinguished by selecting appropriate detection process parameters, such as probe frequency 5 MHz, array elements 36, and probe aperture 16 mm. The research results can provide theoretical reference for the detection of blowout preventer. [ABSTRACT FROM AUTHOR]