Pure and Al-doped (3 at.%) ZnO nanorods were prepared by two-step synthesis. In the first step, ZnO thin films were deposited on silicon wafers by spin coating; then, ZnO nanorods (NR) and Al-doped ZnO NR were grown using a chemical bath method. The structural properties of zincite nanorods were determined by X-ray diffraction (XRD) and corroborated well with the morphologic properties obtained by field-emission gun scanning electron microscopy (FEG SEM) with energy-dispersive X-ray spectroscopy (EDS). Morphology results revealed a minute change in the nanorod geometry upon doping, which was also visible by Kelvin probe force microscopy (KPFM). KPFM also showed preliminary electrical properties. Detailed electrical characterization of pure and Al-doped ZnO NR was conducted by temperature-dependent current-voltage (I-V) measurements on Au/(Al)ZnO NR/n-Si junctions. It was shown that Al doping increases the conductivity of ZnO NR by an order of magnitude. The I-V characteristics of pure and Al-doped ZnO NR followed the ohmic regime for lower voltages, whereas, for the higher voltages, significant changes in electric conduction mechanisms were detected and ascribed to Al-doping. In conclusion, for future applications, one should consider the possible influence of the geometry change of (Al)ZnO NRs on their overall electric transport properties.

Sulfur-doped TiO 2 (S-TiO 2 ) composites with reduced graphene oxide (rGO), wt. % of rGO equal to 0.5%, 2.75%, and 5.0%, were prepared by a one-pot solvothermal procedure. The aim was to improve photocatalytic performance in comparison to TiO 2 under simulated solar irradiation for the treatment of diclofenac (DCF) in aqueous medium. The obtained composites were characterized for physical-chemical properties using thermogravimetric analysis (TGA), X-ray diffractograms (XRD), Raman, scanning electron microscopy (SEM)/energy dispersive X-ray (EDX), Brauner Emmett Teller (BET), and photoluminescence (PL) analyses, indicating successful sulfur doping and inclusion of rGO. Sulfur doping and rGO have successfully led to a decrease in photogenerated charge recombination. However, both antagonistic and synergistic effects toward DCF treatment were observed, with the latter being brought forward by higher wt.% rGO. The composite with 5.0 wt.% rGO has shown the highest DCF conversion at pH 4 compared to that obtained by pristine TiO 2 , despite lower DCF adsorption during the initial dark period. The expected positive effects of both sulfur doping and rGO on charge recombination were found to be limited because of the subpar interphase contact with the composite and incomplete reduction of the GO precursor. Consequent unfavorable interactions between rGO and DCF negatively influenced the activity of the studied S-TiO 2 /rGO photocatalyst under simulated solar irradiation.