Arrays of aligned carbon nanotubes (CNTs) are anisotropic nanomaterials possessing a high length-to-diameter aspect ratio, channels passing through the array, and mechanical strength along with flexibility. The arrays are produced in one step using aerosol-assisted catalytic chemical vapor deposition (CCVD), where a mixture of carbon and metal sources is fed into the hot zone of the reactor. Metal nanoparticles catalyze the growth of CNTs and, during synthesis, are partially captured into the internal cavity of CNTs. In this work, we considered various stages of multi-walled CNT (MWCNT) growth on silicon substrates from a ferrocene-toluene mixture and estimated the amount of iron in the array. The study showed that although the mixture of precursors supplies evenly to the reactor, the iron content in the upper part of the array is lower and increases toward the substrate. The size of carbon-encapsulated iron-based nanoparticles is 20-30 nm, and, according to X-ray diffraction data, most of them are iron carbide Fe 3 C. The reasons for the gradient distribution of iron nanoparticles in MWCNT arrays were considered, and the possibilities of controlling their distribution were evaluated.

Vertically aligned carbon nanotube (CNT) arrays show potential for the development of planar low-voltage emission cathodes. The characteristics of cathodes can be improved by modifying their surface, e.g., by hydrogen plasma treatment, as was performed in this work. The surface of multi-walled CNT arrays grown on silicon substrates from toluene and ferrocene using catalytic chemical vapor deposition was treated in a high-pressure (~10 4 Pa) microwave reactor. The structure, composition, and current-voltage characteristics of the arrays were studied before and after hydrogen plasma treatment at various power values and durations. CNT tips were destroyed and catalytic iron was released from the CNT channels. The etching rate was influenced by iron particles that formed on the array surface. The lower emission threshold in the plasma-treated arrays than in the initial sample is explained by the amplification factor of the local electric field increasing due to graphene structures of unfolded nanotube layers that formed at the CNT tips.

We systematically studied the electromagnetic properties of carbon nanohorns (CNHs) and polystyrene composites filled with CNHs in static regime, low frequency and microwave regions. CNHs were synthesized using the direct current arc-discharge method using solid graphite rods and graphite rods filled by melamine mixed with graphite powder. Transmission electron microscopy and thermo-gravimetric analysis showed that CNH agglomerates are the main product, while the addition of melamine promotes the formation of graphite balls. Graphitic contamination causes the internal leakage of inter-agglomerate capacity, lowering the permittivity and enhancing the conductivity of composites. The permittivity of CNH/polystyrene composites increases with the filler fraction, and near the dielectric threshold electromagnetic characteristics of the composites exhibit critical behaviour. Our results suggest that CNHs with relatively high values of permittivity and contact resistance could be used as high- k materials.