Search

In the present work, the magnetron sputtering technique was used to prepare new catalysts of formic acid electrooxidation based on TiO 2 nanotubes decorated with Pt (platinum), Pd (palladium) or Pd + Pt nanoparticles. TiO 2 nanotubes (TiO 2 NTs) with strictly defined geometry were produced by anodization of Ti foil and Ti mesh in a mixture of glycerol and water with ammonium fluoride electrolyte. The above mentioned catalytically active metal nanoparticles (NPs) were located mainly on the top of the TiO 2 NTs, forming 'rings' and agglomerates. A part of metal nanoparticles decorated also TiO 2 NTs walls, thus providing sufficient electronic conductivity for electron transportation between the metal nanoparticle rings and Ti current collector. The electrocatalytic activity of the TiO 2 NTs/Ti foil, decorated by Pt, Pd and/or Pd + Pt NPs was investigated by cyclic voltammetry (CV) and new Pd/TiO 2 NTs/Ti mesh catalyst was additionally tested in a direct formic acid fuel cell (DFAFC). The results so obtained were compared with commercial catalyst-Pd/Vulcan. CV tests have shown for carbon supported catalysts, that the activity of TiO 2 NTs decorated with Pd was considerably higher than that one decorated with Pt. Moreover, for TiO 2 NTs supported Pd catalyst specific activity (per mg of metal) was higher than that for well dispersed carbon supported commercial catalyst. The tests at DFAFC have revealed also that the maximum of specific power for 0.2 Pd/TiO 2 catalyst was 70% higher than that of the commercial one, Pd/Vulcan. Morphological features, and/or peculiarities, as well as surface composition of the resulting catalysts have been studied by scanning electron microscopy (SEM), scanning transmission electron microscopy (STEM), and chemical surface analytical methods (X-ray photoelectron spectroscopy-XPS; Auger electron spectroscopy-AES)., Competing Interests: The authors declare no conflict of interest.

The aim of this work was to characterize the microstructure of the as-cast Haynes ® 282 ® alloy. Observations and analyses were carried out using techniques such as X-ray diffraction (XRD), light microscopy (LM), scanning electron microscopy (SEM), transmission electron microscopy (TEM), X-ray spectroscopy (EDS), wave length dispersive X-ray spectroscopy (WDS), auger electron spectroscopy (AES) and electron energy-loss spectrometry (EELS). The phases identified in the as-cast alloy include: γ (gamma matrix), γ' (matrix strengthening phase), (TiMoCr)C (primary carbide), TiN (primary nitride), σ (sigma-TCP phase), (TiMo)₂SC (carbosulphide) and a lamellar constituent consisting of molybdenum and chromium rich secondary carbide phase together with γ phase. Within the dendrites the γ' appears mostly in the form of spherical, nanometric precipitates (74 nm), while coarser (113 nm) cubic γ' precipitates are present in the interdendritic areas. Volume fraction content of the γ' precipitates in the dendrites and interdendritic areas are 9.6% and 8.5%, respectively. Primary nitrides metallic nitrides (MN), are homogeneously dispersed in the as-cast microstructure, while primary carbides metallic carbides (MC), preferentially precipitate in interdendritic areas. Such preference is also observed in the case of globular σ phase. Lamellar constituents characterized as secondary carbides/γ phases were together with (TiMo)₂SC phase always observed adjacent to σ phase precipitates. Crystallographic relations were established in-between the MC, σ, secondary carbides and γ/γ' matrix.