Randomized particle distribution in a mixed matrix membrane would reduce the effectiveness of particle immobilized in its matrix. This study aims to distribute the particle near the membrane surface with magnetic field assistance. Specifically, investigating the influence of varied magnetic patterns (rod, chain, and circular) on zinc ferrite distribution in the membrane on the phenol adsorption with the standing time was fixed at 30 s with 12 wt% zinc ferrite. The findings revealed that the magnetic induce membrane possesses the highest phenol adsorption, especially by membrane fabricated by magnets in a circular pattern (MB). MB membrane displayed phenol adsorption capacity of 415 mg/g with water permeation of 30.4 L/m2.h. The high phenol adsorption was contributed to high zinc ferrite particle migrated towards the membrane surface, and EDX analysis revealed 1.23 wt% Fe element in its thin layer region. These findings indicate that the magnets arranged in a circular pattern can effectively migrate and distribute the zinc ferrite across the membrane. Hence, a suitable magnetic pattern was vital when applying magnetic induce casting. [Display omitted] • The magnet in magnetic induced casting was arranged to circular, chain, and rod. • Circular pattern (MB) has the highest phenol adsorption capacity at 415 mg/g. • MB and MC (chain) membrane driven by external diffusion with film thickness Δr o of 5.22 and 16.94 nm. [ABSTRACT FROM AUTHOR]

Tuning the ratio of sp2/sp3 is crucial factor for obtaining high aspect ratio of graphene oxide. In this work, we reported a comprehensive study on synthesis of GO with different sp2/sp3 ratios at different oxidation reaction temperatures. The physicochemical properties of the as-prepared GO were characterized by Attenuated total reflectance infrared spectroscopy (ATR-IR), Raman spectroscopy, Solid-state nuclear magnetic resonance (SSNMR), Field emission scanning electron microscope (FESEM), X-ray diffraction (XRD), Transmission electron microscope (TEM), hydrophilicity test and zeta potential. Interestingly, GO-35 showed the smallest contact angle with carbon-to-oxygen (O/C) ratio 0.469. ATR-IR reveals the different intensity of hydroxyl (−OH), carbonyl (−C O), epoxy (C–O–C), as well as carboxyl (−COOH) moieties in the GO samples, and their intermolecular interactions significantly affected the interlayer spacing between consecutive identical planes of carbon atoms which examined using XRD. XPS confirmed that the basal species such as –OH is abundantly available in the GO-35 and unavailable in GO-50. Our results demonstrate that the properties of GO can be tuned using different oxidation reaction temperatures, which significantly influences types of oxygen-functional groups generated at different oxidation levels, thus could pave the way for various applications of graphene-based material. [Display omitted] • The ratio of sp2/sp3 in the GO structure can be tuned by oxidation temperature. • The integrity of graphene structure greatly decreases at oxidation temperature 50 °C. • Epoxy and hydroxyl species abundantly formed throughout the basal structure at optimum oxidation temperature, 35 °C. [ABSTRACT FROM AUTHOR]