We developed a one-pot strategy to fabricate activated carbons by using water soluble phenol-formaldehyde resin as precursor and Na 2 CO 3 as activating agent. The prepared carbon materials have a typical hierarchical pore texture and a large specific surface area (SSA) of 1357 m 2 g −1 . When used as electrode materials for supercapacitors, the material shows a high specific capacitance of 226 F g −1 at 0.05 A g −1, good rate capability of 62.4% in the range of 0.05–20 A g −1 and outstanding cycling stability (only 2.5% loss in specific capacitance after 5000 cycles). These results suggest a low-cost and environmentally friendly design of electrode materials for high-performance supercapacitors. [ABSTRACT FROM AUTHOR]

Abstract: Porous carbon was prepared from deoiled asphalt by conventional NaOH activation process and by the combination of nano-sized MgO template method and NaOH activation process. The electrochemical properties used as supercapacitors electrode material were evaluated in 7M KOH aqueous solution. Porous carbon sample obtained by NaOH activation possessed more micropores and higher specific surface area, resulting in a higher specific capacitance of 235Fg−1 at low charge–discharge current of 50mAg−1. For the combination method, the resultant carbons possessed higher capacitance and good capacitance maintaining at high current, with a capacitance of nearly twice as that of the former at current density of 10Ag−1, due to their abundant mesopores. [Copyright &y& Elsevier]