Highlights • The electrospinning was developed for fabrication of collagen mimetic scaffold. • With addition of LA, LA assisted formation of 3D cotton-like fibrous structure. • The physicochemical properties of the as-fabricated scaffold were evaluated. Abstract The ability to mimic the topography of aligned collagen fiber bundles (A-CFB) that form the structural basis for the extracellular matrix (ECM) can be an important step in the fabrication of engineered scaffolds. Because the cell adhesion to the surface topography involve cell adhesion localized structures, topographical features, which mimics the A-CFB of the matrix can be a significant factor for cell activities. In this study, we present a novel method for the fabrication of low-density electrospun fibers mimicking A-CFB constructs. The three dimensional (3D) cotton-like A-CFB mimetic scaffold (3D-CACMS) of a mixture of lactic acid (LA) and polycaprolactone (PCL) was prepared by multiple pins rotator electrospinning (MPRES), followed by selective leaching of LA. The results of SEM, FTIR, TGA, and DSC revealed the physicochemical properties of the as-fabricated scaffold. This 3D-CACMS attempt to mimic A-CFB and can potentially meet the requirements for practical use of biomedical engineering. [ABSTRACT FROM AUTHOR]

Electrospinning is not only a technique to fabricate macroscopic fiber but also a method to control the microstructure. In this study, high-temperature solution electrospinning was used to prepare isotactic polypropylene (iPP) fibers. Scanning electron microscope (SEM) observation indicates that a single electrospun iPP fiber consists of many nano-fibrils. Based on SEM observation, these nano-fibrils are shish-kebab structure. Electrostatic elongational force involved in the electrospinning process is considered to be responsible for the development of shish-kebab structure. [ABSTRACT FROM AUTHOR]

Abstract: Porous silica ceramics were successfully prepared from silica spinning solution and introduced silica particles by electrospinning. After sintering, the sample was mainly composed of the introduced silica particles instead of the electrospun ceramic fibers. Therefore, the role of the introduced particles in this work was quite different from that of the introduced fillers in other electrospinning works. The porosity of the samples sintered at 1000°C and 1200°C were 62.4% and 55.6%, respectively. Furthermore, the porosity of the sintered sample can be adjusted by changing the content of the introduced silica particles. This method can be extended to prepare other porous ceramics just by changing the kinds of introduced particles. [Copyright &y& Elsevier]