Search

Abstract The effects of ω precipitates and orthorhombic (α″) martensitic transformation on stress-strain behavior were studied in metastable β Ti-10V-2Fe-3Al alloy single-crystal in submicron scales. We successfully distinguished the size effects induced by ω precipitates and α″ phase transformation through compressing the metastable β Ti-10V-2Fe-3Al along the orientation of <011> β , which is unfavorable for α″ phase transformation. Two individual exponential curves express well the relationship between the strengthening exponents, which were regressed using the flow stresses at different ranges of plastic strains of 0.2–13% and the pillar widths, and the corresponding plastic strain. It is worth noting that the strengthening exponent jumps from 0.256 to 0.293 at 8% plastic strain. Double size effects are uncovered in metastable β Ti-10V-2Fe-3Al alloy single-crystal micropillars. The first (ω precipitate-related) size effect has been predicted with the proposed models, and the second (martensitic transformation-induced) size effect is interpreted with the modified Liu's equation. [ABSTRACT FROM AUTHOR]

Abstract Double size effects are uncovered in metastable β Ti-10V-2Fe-3Al alloy single-crystal micropillars subjected to compress along <011> β in the Part I of this paper. In this Part II, a series of samples at different deformation stages were systematically analyzed by transmission electron microscopy (TEM) to understand the deformation mechanism for double size effects. Two distinct phase transformations were observed to take place at different stages of plastic deformation. In the initial stage, dislocation interaction with ω precipitates and deformation-induced ω variants transformation from one to another are predominant plastic deformation mechanisms when the total strain is less than 10%. As a result, high density of ω precipitates contributes to the weak size effect and the continuous stable strain-hardening behavior in the metastable β Ti-10V-2Fe-3Al alloy. In comparison, the martensitic transformation from β to α″ is induced when the critical strain reaches to 10%. The strain-induced martensitic transformation becomes primary deformation modes, which result in higher strain-hardening exponent and stronger size effect, in the second deformation stage. These results provide a new perspective of designing micro-electromechanical materials with an excellent combination of the enhanced yield strength and stable plasticity. [ABSTRACT FROM AUTHOR]

Deformed coarse-grained polycrystalline metals always unload elastically where permanent dislocation network well-developed in the loading regime hinders the movement of dislocations and allows only the elastic relaxation of stress. Such elastic unloading behavior is, however, unexpected in nanocrystalline metals because the dislocation network cannot effectively form inside nanometer-scale grains. In this work, we report the experimental finding of significant plastic deformation that emerges in the unloading regime in the compressive cyclic test at room temperature of nanocrystalline Cu. The magnitude of plastic strain produced during unloading depends strongly on loading and unloading rates. This plastic unloading behavior arises from the rapid absorption of dislocations accumulated during loading, which was quantitatively interpreted by performing the incremental unloading test and developing a relationship between the dislocation density and the loading and unloading rates based on the models of the statistical absorption of dislocations by grain boundaries and the dislocation emission from grain boundary ledges. Concurrently, the evolution of deformation structures during the cyclic deformation was also analyzed in terms of the interactions of gliding dislocation–twin boundaries. [ABSTRACT FROM AUTHOR]

A novel metastable β-Ti alloy based on Ti–Al–Zr–Mo–Cr system was successfully designed and fabricated. Superior combination of high strength (UTS = 1534-1198 MPa) and ductility (El = 7.0%–20.9%) is achieved in this alloy. After high reduction β transus forging and subsequent heat treatment, a multi-scale distribution of α phase is displayed which contains micro-scale elongated primary α (α p), sub-micro α rod (α r) and nano-sized α platelets (α s). Detailed selected area electron diffraction (SAED) pattern and high resolution-TEM analysis show the production of FCC substructure inside α p and α r with an orientation relationship of <0001> hcp //<001> fcc , {11 2 ‾ 0} hcp //{ 2 ‾ 20} fcc , {10 1 ‾ 0} hcp //{220} fcc. Two variants of FCC lamella are discovered which is related by a 120° rotation around <001> axis. The effect of microstructure on the improved strength-ductility combination is briefly discussed. Both FCC lamella and multi-scale distribution of α phase could create an effective strain partition during plastic deformation and increase the ductility. High strength originates from the distribution of high fraction nano-scaled α s which could effectively hinder dislocation slip in β matrix. [ABSTRACT FROM AUTHOR]