Abstract: The effect of Al–P–Ti–TiC–Nd2O3 modifier on the microstructure and mechanical properties of hypereutectic Al–20wt.%Si alloy has been investigated. It has been concluded that Nd2O3 in Al–P–Ti–TiC–Nd2O3 modifier can modify primary silicon in hypereutectic Al–Si alloys. Statistical analysis shows that primary silicon size (approximately average 38μm) in modified Al–20wt.%Si alloy with Al–P–Ti–TiC modifier is larger than that (approximately average 20μm) in modified Al–20wt.%Si alloy with Al–P–Ti–TiC–Nd2O3 modifier. Compared with primary silicon modified with Al–P–Ti–TiC modifier, Primary silicon modified with Al–P–Ti–TiC–Nd2O3 modifier has the smaller size at different holding times such as 10, 60 and 120min. The internal defects in coarser primary silicon particles play an important role in determining the tensile strength and elongation of the materials. Coarser primary silicon particles in unmodified Al–Si alloys can degrade the loading bearing capacity of the materials. Modification can eliminate the internal defects to a great extent and improve the tensile strength and elongation of hypereutectic Al–Si alloys. Compared with unmodified and heat-treated Al–20wt.%Si alloy, the tensile strength of the modified with Al–P–Ti–TiC–Nd2O3 modifier and heat-treated Al–20wt.%Si alloy increases by 20%. [Copyright &y& Elsevier]

A TiB2 particulate reinforced magnesium matrix composite (MMCs) was fabricated by adding a TiB2–Al master alloy processed via self-propagating high-temperature synthesis (SHS) reaction in Al–Ti–B system into molten magnesium and using the stir casting technique. The results showed that the TiB2–Al master alloy and TiB2/Mg composite contained a certain amount of transient TiAl3 phase. When the Al–Ti–B system was incorporated with an appropriate C, TiB2 and TiC reinforcing phases were simultaneously synthesized and the TiAl3 phase was almost completely eliminated. [Copyright &y& Elsevier]