In order to obtain an ideal material using for artificial corneal skirt, a porous polymer hydrogel containing 2-hydroxyethyl methacrylate (HEMA), trimethylolpropane triacrylate (TMPTA) and butyl acrylate was prepared through one-step radical polymerization method and the usage of CaCO 3 whisker as porogen. The physical-chemical properties of the fabricated polymer hydrogel can be adjusted by CaCO 3 whisker content, such as pore size, porosity, water content of materials and surface topography. Then a series of cell biology experiments of human corneal fibroblasts (HCFs) were carried out to evaluate its properties as an artificial corneal skirt, such as the adhesion of cells on the materials with different pore size and porosity, the apoptosis on materials with different characteristics, the distribution of the cells on the material surface. The results revealed that high porosity not only could improve water content of hydrogel, but also strengthen the adhesion of HCFs on hydrogel. In addition, high porosity hydrogel with the whisker shape of pores showed much elongate spindle-like morphology than those low porosity hydrogels. MTT assay certified that the resulted polymer hydrogel material possessed excellent biocompatibility and was suitable for HCFs growing, making it promising for being developed as artificial corneal skirt. [ABSTRACT FROM AUTHOR]

Superhydrophobic coatings were successfully fabricated by photo-crosslinked polyurethane (PU) and organic fluoro group-functionalized SiO 2 nanoparticles (F-SiO 2 NPs), and were introduced for preventing microleakage in a dental composite restoration. The F-SiO 2 NPs possessed low surface energy and the PU can not only improve the mechanical stability but also promote F-SiO 2 NPs to form multiscale structure, which could facilitate the properties of the as-prepared superhydrophobic coating by synergetic effect. The morphology and properties of the resulted superhydrophobic coatings with different PU/F-SiO 2 ratios were studied using 1 H NMR spectrum, fourier transform infrared spectra, scanning electron microscopy, atomic force microscopy and UV–vis spectrophotometry. The results showed that the superhydrophobic coatings with low PU/F-SiO 2 ratio (1:3) possessed excellent hierarchical papillae structure with trapped air pockets, high contact angle (160.1°), low sliding angle (< 1°) and good transparency. Additionally, MTT experiments results certified the prominent cell viability and biocompatibility for clinical application. Based on its fantastically superhydrophobic property, the as-prepared superhydrophobic coatings effectively prevented water permeation in resin composite restoration evaluation. This research may provide an effective method to solve the problem of microleakage and will efficiently increase the success rate of dental composite restorations. [ABSTRACT FROM AUTHOR]