In this study, a strategy of using iodine-containing cyclophosphazenes as radiopacifiers for dental composite resin was evaluated. It was hypothesized that cyclophosphazenes bearing both iodine and acrylate group swere able to endow composite resins radiopacity without compromising mechanical properties. The cyclophosphazene compounds were synthesized by subsequently nucleophilic substitution of hexachlorocyclotriphosphazene with hydroxyethyl methacrylate (HEMA) and 4-iodoaniline. Cyclotriphosphazenes containing two different molar ratios of HEMA to 4-iodoaniline (1:5 and 2:4) were obtained, and were identified with 1 H NMR, FT-IR, UV and mass spectroscopy. The iodine-containing cyclophosphazenes were able to dissolve well in bisphenol A glycidyl methacrylate (Bis-GMA)/triethylene glycol dimethacrylate (TEGDMA) resin, and were added at two contents (10 or 15%wt. of the resin). The resins were photo-cured and post-thermal treated before characterizations. The resulting composite resins demonstrated the ability of blocking X-ray. And the addition of HEMA-co-iodoaniline substituted cyclotriphosphazenes caused minor adverse effect on the mechanical properties of the resins because the cyclotriphosphazenes could mix well and react with the resins. The presence of rigid phosphazene rings between resin backbones displayed an effective function of decreasing polymerization shrinkage. In summary, soluble and reactive iodine-containing cyclotriphosphazenes demonstrated advantages over traditional heavy metals or metal oxides in being used as additives for producing radiopaque dental resins. [ABSTRACT FROM AUTHOR]

Abstract: A kind of core–shell nanofibers containing sodium fluoride (NaF) was produced and used as reinforcing materials for dimethacrylate-based dental restorative resins in this study. The core–shell nanofibers were prepared by coaxial-electrospinning with polyacrylonitrile (PAN) and poly(methyl methacrylate) (PMMA) solutions as core and shell fluids, respectively. The produced PAN–PMMA nanofibers varied in fiber diameter and the thickness of PMMA shell depending on electrospinning parameters. NaF-loaded nanofibers were obtained by incorporating NaF nanocrystals into the core fluid at two loadings (0.8 or 1.0wt.%). Embedment of NaF nanocrystals into the PAN core did not damage the core–shell structure. The addition of PAN–PMMA nanofibers into Bis-GMA/TEGDMA clearly showed the reinforcement due to the good interfacial adhesion between fibers and resin. The flexural strength (Fs) and flexural modulus (Ey) of the composites decreased slightly as the thickness of PMMA shell increasing. Sustained fluoride releases with minor initial burst release were achieved from NaF-loaded core–shell nanofibers and the corresponding composites, which was quite different from the case of embedding NaF nanocrystals into the dental resin directly. The study demonstrated that NaF-loaded PAN–PMMA core–shell nanofibers were not only able to improve the mechanical properties of restorative resin, but also able to provide sustained fluoride release to help in preventing secondary caries. [Copyright &y& Elsevier]