The relationship between the viscosity and the electrical conductivity of CaF2-SiO2- Al2O3-CaO-MgO slag system was deduced through theoretical calculation and experiment. The experiment was designed by quadratic orthogonal rotary regression method. The slag viscosity and conductivity were measured at 1600, and the constant (C) was calculated. The calculating model between each component mass fraction and constant C was performed, and the stability of calculating model was also verified by representative slag. The results showed that the calculating constant (C) of regression model is in good agreement with experimental values. Thus, the relationship between refining slag viscosity and conductivity using the formula at certain temperature is feasible.

The slurry erosion wear performances of the SiCp/cast iron surface composite, which was prepared by infiltrating molten cast iron into SiC particles preforms, were studied on self-made slurry inject erosion wear machine. The results show that the erosion wear rate of the SiCp/cast iron surface composite would be the lowest at impact angle of 30°, and the largest at impact angle of 60°. The erosion wear rate increases gradually when impact angle is changed from 30° to 60°, and then decreased with increasing the impact angle. The erosion wear mechanism of the SiCp/cast iron surface composite is dominated by cutting and grooving at low impact angle, and by fatigue spalling and cutting at high impact angle. For the gray cast iron, the erosion wear rate of would be increased gradually with the increase of impact angle, reaching the peak value at 90°, which indicates the typical characteristics of brittle material in slurry erosion wear process.

Titanium silicon carbide (Ti3SiC2) is a remarkable material for its combination of the best properties of metals and ceramics. The high purity Ti3SiC2 ceramic has been prepared by infiltration sintering (IS), and the effect of a small amount of Si on Ti3SiC2 ceramic formation was investigated. The results show that the purity of Ti3SiC2 ceramic could be increased significantly and the sintering time for Ti3SiC2 could be decreased remarkably when proper amount of Si was added in the starting mixture. The Ti3SiC2 sintered compact with a purity of 99.2wt% and a relative density of 97% was obtained by the infiltration sintering from a starting mixture composed of n(Ti):n(Si):n(TiC) = 1:0.3:2 at 1500 °C with holding time of 2/3h.