Search

The effect of the amount of desorbed water on the mechanical properties of composites based on low-density polyethylene and linen yarn production waste (LW) is analyzed by statistical methods. It is shown that the amount of absorbed water decreases during the desorption process at room temperature both for specimens modified and unmodified with diphenylmethane diisocyanate (DIC.) The most sensitive to the action of water is the elastic modulus, which decreases considerably under the effect of water and is fully restored in the desorption process. The tensile strain also increases with the amount of absorbed water. It is found that the elastic modulus of the unmodified composite correlates linearly with the amount of desorbed water. Between the amount of desorbed water and the tensile strain, as well the specific work of deformation, a negative linear correlation is revealed. After water desorption, all strength and deformation characteristics of both the modified and unmodified composites are fully recovered.

The possibilities of using various methods of mathematical statistics for processing and analyzing the results of deformation and strength tests on composites made from a low-density polyethylene and linen yarn production waste are evaluated. The hypothesis that the experimental strength data agree with the Gaussian distribution is examined by the Shapiro–Wilk test (W-test.) It is shown that the Gaussian distribution, both for systems unmodified and modified with diphenylmethane diisocyanate (DIC), is valid only for two parameters: the maximum tensile strength σmax and the elastic modulus Et. For the other parameters (the relative elongation emax corresponding to σmax, the specific total work of failure Ab), and the specific work of failure to the tensile strength Amax), a non-Gaussian distribution is observed. An analysis of measurements for different specimens by the Bartlett test shows that the Et data have equal variances for both systems (with and without DIC), but for the system containing DIC, the σmax data have different variances. A two-factor ANOVA analysis reveals that DIC considerably affects the tensile strength and modulus of composites, but the influence of test conditions is a statistically significant factor only for the modulus. The coefficient of variation is considerably lower for σmax than for Et and can be used as a quantitative measure for the degree of heterogeneity of the composites investigated.

The effect of the amount of absorbed water on the physicomechanical indices (tensile modulus, tensile strength, and ultimate strain) of composites based on secondary polyethylene (SPE) of two trademarks and linen yarn production waste (LW), both with and without a coupling agent (diphenylmetane diisocyanate - DIC), is evaluated. It is shown that the strength properties considerably depend on the time of water sorption and on the blend composition. The tensile strength decreases with increased amount of absorbed water (with increased time of exposure to distilled water) and with increased content of LW in the composites. This can be explained by the plasticizing effect of water molecules, which is confirmed by the increase in the ultimate strain of specimens after their exposure to water. The slight increase in the strength observed for the systems modified with DIC is probably caused by cross-linking of the free diisocyanate in the system under the action of moisture. The diisocyanate intensifies the interfacial interaction and retards the water-sorption process. Therefore, the resulting strength indices of these systems are higher than those of the unmodified compositions.