Search

In this study, polypropylene porous membranes with an average pore size of 1.25 µm were modified by barrier discharge plasma. Next, molecularly imprinted layers with an imprint of diethyl phthalate (DEP) ware grafted of their surface. In order to optimize the composition of the modifying mixture various solvents, the ratios of functional monomers and the cross-linking monomer as well as various amounts of phthalate were verified. It was shown that the most effective membranes were obtained during polymerization in n-octane with the participation of functional monomers in the ratio 3:7 and the amount of phthalate 7 wt.%. The membranes were tested in the filtration process as well as static and dynamic sorption. In all of these processes, the imprinted membranes showed better properties than those without the imprint. The diethyl phthalate retention coefficient was 36.12% for membranes with a grafting yield of 1.916 mg/cm2. On the other hand, DEP static sorption for the imprinted membranes was 3.87 µmol/g higher than for non-imprinted membranes. Also, in the process of dynamic sorption higher values were observed for membranes with the imprint (DSMIM, 4.12 µmol/g; DSNIM, 1.18 µmol/g). The membranes were also tested under real conditions. In the process of filtration of tap water contaminated with phthalate, the presence of imprints in the membrane structure resulted in more than three times higher sorption values (3.09 µmol/g) than in the case of non-imprinted membranes (1.12 µmol/g).

The mass production of lithium-ion batteries and lithium-rich e-products that are required for electric vehicles, energy storage devices, and cloud-connected electronics is driving an unprecedented demand for lithium resources. Current lithium production technologies, in which extraction and purification are typically achieved by hydrometallurgical routes, possess strong environmental impact but are also energy-intensive and require extensive operational capabilities. The emergence of selective membrane materials and associated electro-processes offers an avenue to reduce these energy and cost penalties and create more sustainable lithium production approaches. In this review, lithium recovery technologies are discussed considering the origin of the lithium, which can be primary sources such as minerals and brines or e-waste sources generated from recycling of batteries and other e-products. The relevance of electro-membrane processes for selective lithium recovery is discussed as well as the potential and shortfalls of current electro-membrane methods.

This paper shows the investigation for the optimal anion exchange membranes (AEM) supporting the desorption step of the HCDI process. The chemical modification of PVDF by diethylene triamine created the AEM. To confirm the ion-exchange character of materials, the chemical analysis with FTIR, SEM, surface energetics, and transportation analysis were applied. Next, the investigated membranes were applied for the sorption and desorption of lithium chloride. The specific sorptive parameters were higher according to the incorporation of the nitrogen groups into polymeric chains. Considering the desorption efficiency, membranes modified by four days were selected for further evaluation. The application in the HCDI process allowed reaching the desorption efficiency at 90%. The system composed of PVDF-DETA4 membrane was suitable for sorption 30 mg/g of salt. By applying the PVDF-DETA4 membrane, it is possible to concentrate LiCl with four factors. The anion exchange character of the developed membrane was confirmed by adsorption kinetics and isotherms of chlorides, nitrates, sodium, and lithium. The prepared membrane could be considered a perspective material suitable for concentration salt with electro-driven technologies for the above reasons.