The main objective of this work is to demonstrate and validate the feasibility of fabricating (Al, In) GaN laser diodes with etched facets. The facets are fabricated using a two-step dry and wet etching process: inductively coupled plasma—reactive ion etching in chlorine, followed by wet etching in tetramethylammonium hydroxide (TMAH). For the dry etching stage, an optimized procedure was used. For the wet etching step, the TMAH temperature was set to a constant value of 80 °C, and the only variable parameter was time. The time was divided into individual steps, each of 20 min. To validate the results, electro-optical parameters were measured after each step and compared with a cleaved reference, as well as with scanning electron microscope imaging of the front surface. It was determined that the optimal wet etching time was 40 min. For this time, the laser tested achieved a fully comparable threshold current (within 10%) with the cleaved reference. The described technology is an important step for the future manufacturing of photonic integrated circuits with laser diodes integrated on a chip and for ultra-short-cavity lasers.

In this study, we propose a solution for realization of surface emitting, 2D array of visible light laser diodes based on AlInGaN semiconductors. The presented system consists of a horizontal cavity lasing section adjoined with beam deflecting section in the form of 45° inclined planes. They are placed in the close vicinity of etched vertical cavity mirrors that are fabricated by Reactive Ion Beam Etching. The principle of operation of this device is confirmed experimentally; however, we observed an unexpected angular distribution of reflected rays for the angles lower than 45°, which we associate with the light diffraction and interference between the vertical and deflecting mirrors. The presented solution offers the maturity of edge-emitting laser technology combined with versatility of surface-emitting lasers, including on-wafer testing of emitters and addressability of single light sources.