Search

Supercritical carbon dioxide (SCCO2) is a non-toxic and environmentally friendly fluid and has been used in polymerization reactions, processing, foaming, and plasticizing of polymers. Exploring the behavior and data of SCCO2 sorption and dissolution in polymers provides essential information for polymer applications. This study investigated the sorption and diffusion of SCCO2 into polyetherimide (PEI). The sorption and desorption processes of SCCO2 in PEI samples were measured in the temperature range from 40 to 60 °C, the pressure range from 20 to 40 MPa, and the sorption time from 0.25 to 52 h. This study used the ex situ gravimetric method under different operating conditions and applied the Fickian diffusion model to determine the mass diffusivity of SCCO2 during sorption and desorption processes into and out of PEI. The equilibrium mass gain fraction of SCCO2 into PEI was reported from 9.0 wt% (at 60 °C and 20 MPa) to 12.8 wt% (at 40 °C and 40 MPa). The sorption amount increased with the increasing SCCO2 pressure and decreased with the increasing SCCO2 temperature. This study showed the crossover phenomenon of equilibrium mass gain fraction isotherms with respect to SCCO2 density. Changes in the sorption mechanism in PEI were observed when the SCCO2 density was at approximately 840 kg/m3. This study qualitatively performed FTIR analysis during the SCCO2 desorption process. A CO2 antisymmetric stretching mode was observed near a wavenumber of 2340 cm−1. A comparison of loss modulus measurements of pure and SCCO2-treated PEI specimens showed the shifting of loss maxima. This result showed that the plasticization of PEI was achieved through the sorption process of SCCO2. [ABSTRACT FROM AUTHOR]

Transition metal oxides (TMOs) are important anode materials in sodium-ion batteries (SIBs) due to their high theoretical capacities, abundant resources, and cost-effectiveness. However, issues such as the low conductivity and large volume variation of TMO bulk materials during the cycling process result in poor electrochemical performance. Nanosizing and compositing with carbon materials are two effective strategies to overcome these issues. In this study, spherical MnFe2O4@xC nanocomposites composed of MnFe2O4 inner cores and tunable carbon shell thicknesses were successfully prepared and utilized as anode materials for SIBs. It was found that the property of the carbon shell plays a crucial role in tuning the electrochemical performance of MnFe2O4@xC nanocomposites and an appropriate carbon shell thickness (content) leads to the optimal battery performance. Thus, compared to MnFe2O4@1C and MnFe2O4@8C, MnFe2O4@4C nanocomposite exhibits optimal electrochemical performance by releasing a reversible specific capacity of around 308 mAh·g−1 at 0.1 A·g−1 with 93% capacity retention after 100 cycles, 250 mAh·g−1 at 1.0 A g−1 with 73% capacity retention after 300 cycles in a half cell, and around 111 mAh·g−1 at 1.0 C when coupled with a Na3V2(PO4)3 (NVP) cathode in a full SIB cell. [ABSTRACT FROM AUTHOR]

According to our recent studies on hydrophobicity, this work is aimed at understanding the dependence of hydrophobic interactions on the shape of a solute's surface. It has been observed that dissolved solutes primarily affect the structure of interfacial water, which refers to the top layer of water at the interface between the solute and water. As solutes aggregate in a solution, hydrophobic interactions become closely related to the transition of water molecules from the interfacial region to the bulk water. It is inferred that hydrophobic interactions may depend on the shape of the solute surface. To enhance the strength of hydrophobic interactions, the solutes tend to aggregate, thereby minimizing their surface area-to-volume ratio. This also suggests that hydrophobic interactions may exhibit directional characteristics. Moreover, this phenomenon can be supported by calculated potential mean forces (PMFs) using molecular dynamics (MD) simulations, where different surfaces, such as convex, flat, or concave, are associated with a sphere. Furthermore, this concept can be extended to comprehend the molecular packing parameter, commonly utilized in studying the self-assembly behavior of amphiphilic molecules in aqueous solutions. [ABSTRACT FROM AUTHOR]

This study details the rational design and synthesis of Cu2ZnSnS4 (CZTS)-doped anatase (A) heterostructures, utilizing earth-abundant elements to enhance the efficiency of solar-driven water splitting. A one-step hydrothermal method was employed to fabricate a series of CZTS–A heterojunctions. As the concentration of titanium dioxide (TiO2) varied, the morphology of CZTS shifted from floral patterns to sheet-like structures. The resulting CZTS–A heterostructures underwent comprehensive characterization through photoelectrochemical response assessments, optical measurements, and electrochemical impedance spectroscopy analyses. Detailed photoelectrochemical (PEC) investigations demonstrated notable enhancements in photocurrent density and incident photon-to-electron conversion efficiency (IPCE). Compared to pure anatase electrodes, the optimized CZTS–A heterostructures exhibited a seven-fold increase in photocurrent density and reached a hydrogen production efficiency of 1.1%. Additionally, the maximum H2 production rate from these heterostructures was 11-times greater than that of pure anatase and 250-times higher than the original CZTS after 2 h of irradiation. These results underscore the enhanced PEC performance of CZTS–A heterostructures, highlighting their potential as highly efficient materials for solar water splitting. Integrating Cu2ZnSnS4 nanoparticles (NPs) within TiO2 (anatase) heterostructures implied new avenues for developing earth-abundant and cost-effective photocatalytic systems for renewable energy applications. [ABSTRACT FROM AUTHOR]

A series of NH2-functionalized nano-sized magnetic metal–organic frameworks (MOFs) were prepared in this study for Cr(VI) removal from wastewater. It was observed that not only the morphological, i.e., orientation growth of N-doped and iron-based metal–organic frameworks, but also the adsorption of magnetic MOFs is largely related to the used amount of ammonium hydroxide in preparation. For example, with increasing amounts of ammonium hydroxide used in preparation, the morphology of magnetic MOFs changed from spherical to cube and triangular cone. Moreover, the maximum adsorption capacity of spherical-magnetic MOFs, cubic-magnetic MOFs and triangular cone-magnetic MOFs could be up to 204.08 mg/g, 232.56 mg/g and 270.27 mg/g, respectively. Under optimal conditions, the adsorption process of magnetic MOFs for Cr(VI) was consistent with the pseudo-second-order rate equation (R2 = 1) and Langmuir isotherm model (R2 > 0.99). Therefore, magnetic MOFs developed in this work offered a viable option for the removal of Cr(VI) from wastewater. [ABSTRACT FROM AUTHOR]

The difficulty of exposing active sites and easy recombination of photogenerated carriers have always been two critical problems restricting the photocatalytic activity of g-C3N4. Herein, a simple (NH4)2MoO4-induced one-step calcination method was successfully introduced to transform bulk g-C3N4 into g-C3N4/MoO2 composites with a large specific surface area. During the calcination, with the assistance of NH3 and water vapor produced by ammonium molybdate, the pyrolytical oxidation and depolymerization of a g-C3N4 interlayer were accelerated, finally realizing the exfoliation of the g-C3N4. Furthermore, another pyrolytical product of ammonium molybdate was transformed into MoO2 under an NH3 atmosphere, which was in situ loaded on the surface of a g-C3N4 nanosheet. Additionally, the results of photocatalytic hydrogen evolution under visible light show that the optimal g-C3N4/MoO2 composite has a high specific surface area and much improved performance, which is 4.1 times that of pure bulk g-C3N4. Such performance improvement can be attributed to the full exposure of active sites and the formation of abundant heterojunctions. However, with an increasing feed amount of ammonium molybdate, the oxidation degree of g-C3N4 was enhanced, which would widen the band gap of g-C3N4, leading to a weaker response ability to visible light. The present strategy will provide a new idea for the simple realization of exfoliation and constructing a heterojunction for g-C3N4 simultaneously. [ABSTRACT FROM AUTHOR]