Search

As a common two-dimensional carbon material, graphene has been widely doped into polymers to prepare high-performance dielectric materials. However, the shortcomings of graphene, such as large specific surface area and poor dispersion, limit its further application. Therefore, in this work, to solve the problem regarding the uniform dispersion of graphene in the matrix, in situ polymerization was used to prepare graphene/polyimide films, in which 1,4-diiodobutane was used as a reduction agent to prevent the aggregation of graphene oxide (GO) during imidization. High dielectric constant composite films were obtained by adjusting the ratio of 1,4-diiodobutane in GO. The results show that the resulting graphene/polyimide composite film possessed a dielectric constant of up to 197.5, which was more than 58 times higher than that of the polyimide (PI) film. Furthermore, compared to the pure PI film, the composite films showed better thermal stability and mechanical properties. Thermal performance tests showed that the 1,4-diiodobutane added during the preparation of the composite film was thermally decomposed, and there was no residue. We believe our preparation method can be extended to other high dielectric composite films, which will facilitate their further development and application in high power density energy storage materials. [ABSTRACT FROM AUTHOR]

In terms of new-generation energy-storing devices, aqueous zinc-ion batteries (AZIBs) are becoming the prime candidates because of their inexpensive nature, inherent safety, environmental benignity and abundant resources. Nevertheless, due to a restrained selection of cathodes, AZIBs often perform unsatisfactorily under long-life cycling and high-rate conditions. Consequently, we propose a facile evaporation-induced self-assembly technique for preparing V2O3@carbonized dictyophora (V2O3@CD) composites, utilizing economical and easily available biomass dictyophora as carbon sources and NH4VO3 as metal sources. When assembled in AZIBs, the V2O3@CD exhibits a high initial discharge capacity of 281.9 mAh g−1 at 50 mA g−1. The discharge capacity is still up to 151.9 mAh g−1 after 1000 cycles at 1 A g−1, showing excellent long-cycle durability. The extraordinary high electrochemical effectiveness of V2O3@CD could be mainly attributed to the formation of porous carbonized dictyophora frame. The formed porous carbon skeleton can ensure efficient electron transport and prevent V2O3 from losing electrical contact due to volume changes caused by Zn2+ intercalation/deintercalation. The strategy of metal-oxide-filled carbonized biomass material may provide insights into developing high-performance AZIBs and other potential energy storage devices, with a wide application range. [ABSTRACT FROM AUTHOR]

Materials with outstanding mechanical properties and excellent dielectric properties are increasingly favored in the microelectronics industry. The application of polyimide (PI) in the field of microelectronics is limited because of the fact that PI with excellent mechanical properties does not have special features in the dielectric properties. In this work, PI composite films with high dielectric properties and excellent mechanical properties are fabricated by in-situ reduction of fluorinated graphene (FG) in polyamide acid (PAA) composites. The dielectric permittivity of pure PI is 3.47 and the maximum energy storage density is 0.664 J/cm3 at 100 Hz, while the dielectric permittivity of the PI composite films reaches 235.74 under the same conditions, a 68-times increase compared to the pure PI, and the maximum energy storage density is 5.651, a 9-times increase compared to the pure PI films. This method not only solves the problem of the aggregation of the filler particles in the PI matrix and maintains the intrinsic excellent mechanical properties of the PI, but also significantly improves the dielectric properties of the PI. [ABSTRACT FROM AUTHOR]