Search

As a common two-dimensional carbon material, graphene has been widely doped into polymers to prepare high-performance dielectric materials. However, the shortcomings of graphene, such as large specific surface area and poor dispersion, limit its further application. Therefore, in this work, to solve the problem regarding the uniform dispersion of graphene in the matrix, in situ polymerization was used to prepare graphene/polyimide films, in which 1,4-diiodobutane was used as a reduction agent to prevent the aggregation of graphene oxide (GO) during imidization. High dielectric constant composite films were obtained by adjusting the ratio of 1,4-diiodobutane in GO. The results show that the resulting graphene/polyimide composite film possessed a dielectric constant of up to 197.5, which was more than 58 times higher than that of the polyimide (PI) film. Furthermore, compared to the pure PI film, the composite films showed better thermal stability and mechanical properties. Thermal performance tests showed that the 1,4-diiodobutane added during the preparation of the composite film was thermally decomposed, and there was no residue. We believe our preparation method can be extended to other high dielectric composite films, which will facilitate their further development and application in high power density energy storage materials. [ABSTRACT FROM AUTHOR]

With the increasing pollution of electromagnetic (EM) radiation, it is necessary to develop low-cost, renewable electromagnetic interference (EMI) shielding materials. Herein, wood-derived carbon (WC) materials for EMI shielding are prepared by one-step carbonization of renewable wood. With the increase in carbonization temperature, the conductivity and EMI performance of WC increase gradually. At the same carbonization temperature, the denser WC has better conductivity and higher EMI performance. In addition, due to the layered superimposed conductive channel structure, the WC in the vertical-section shows better EMI shielding performance than that in the cross-section. After excluding the influence of thickness and density, the specific EMI shielding effectiveness (SSE/t) value can be calculated to further optimize tree species. We further discuss the mechanism of the influence of the microstructure of WC on its EMI shielding properties. In addition, the lightweight WC EMI material also has good hydrophobicity and heat insulation properties, as well as good mechanical properties. [ABSTRACT FROM AUTHOR]

Recently, the sustainable utilization of waste resources has become a low-cost and effective strategy to design high-performance functional materials to solve the increasingly serious environmental pollution problem. Herein, the flexible and highly stretchable polyurethane (PU) composite foams assisted by one-dimensional carbon nanotubes (CNTs) and zero-dimensional Fe3O4 were fabricated using waste tire rubbers (WTRs) as reinforcements during a simple self-foaming process. The collaborative introduction of conductive CNTs, magnetic Fe3O4, and WTRs with three-dimensional cross-linked structures enabled the construction of an efficient electronic transmission path and heterointerfaces inside the composite foam. The resulting composite foam possessed a desired minimum reflection loss (RLmin) of −47.43 dB, and also exhibited superior mechanical properties with a tensile strength of >3 MPa and multiple tensile deformation recovery abilities. In addition, increasing the temperature could significantly improve the electromagnetic wave absorption performance of the composite foam. This comprehensive composite foam derived from WTRs has shown a promising development potential for using waste materials to relieve electromagnetic pollution. [ABSTRACT FROM AUTHOR]