Search

In this work, applications of nanohybrid composites based on titanium dioxide (TiO2) with anatase crystallin phase and single-walled carbon nanohorns (SWCNHs) as promising catalysts for the photodegradation of amoxicillin (AMOX) are reported. In this order, TiO2/SWCNH composites were prepared by the solid-state interaction of the two chemical compounds. The increase in the SWCNH concentration in the TiO2/SWCNH composite mass, from 1 wt.% to 5 wt.% and 10 wt.% induces (i) a change in the relative intensity ratio of the Raman lines located at 145 and 1595 cm−1, which are attributed to the Eg(1) vibrational mode of TiO2 and the graphitic structure of SWCNHs; and (ii) a gradual increase in the IR band absorbance at 1735 cm−1 because of the formation of new carboxylic groups on the SWCNHs' surface. The best photocatalytic properties were obtained for the TiO2/SWCNH composite with a SWCNH concentration of 5 wt.%, when approx. 92.4% of AMOX removal was achieved after 90 min of UV irradiation. The TiO2/SWCNH composite is a more efficient catalyst in AMOX photodegradation than TiO2 as a consequence of the SWCNHs' presence, which acts as a capture agent for the photogenerated electrons of TiO2 hindering the electron–hole recombination. The high stability of the TiO2/SWCNH composite with a SWCNH concentration of 5 wt.% is proved by the reusing of the catalyst in six photodegradation cycles of the 98.5 μM AMOX solution, when the efficiency decreases from 92.4% up to 78%. [ABSTRACT FROM AUTHOR]

The aim of this work is to highlight the influence of blends based on TiO2 nanoparticles and reduced graphene oxide (RGO) on the photodegradation of acetaminophen (AC). To this end, the catalysts of TiO2/RGO blends with RGO sheet concentrations equal 5, 10, and 20 wt. % were prepared by the solid-state interaction of the two constituents. The preferential adsorption of TiO2 particles onto the RGO sheets' surfaces via the water molecules on the TiO2 particle surface was demonstrated by FTIR spectroscopy. This adsorption process induced an increase in the disordered state of the RGO sheets in the presence of the TiO2 particles, as highlighted by Raman scattering and scanning electron microscopy (SEM). The novelty of this work lies in the demonstration that TiO2/RGO mixtures, obtained by the solid-phase interaction of the two constituents, allow an acetaminophen removal of up to 95.18% after 100 min of UV irradiation. This TiO2/RGO catalyst induced a higher photodegradation efficiency of AC than TiO2 due to the presence of RGO sheets, which acted as a capture agent for the photogenerated electrons of TiO2, hindering the electron–hole recombination. The reaction kinetics of AC aqueous solutions containing TiO2/RGO blends followed a complex first-order kinetic model. Another novelty of this work is the demonstration of the ability of PVC membranes modified with Au nanoparticles to act both as filters for the removal of TiO2/RGO blends after AC photodegradation and as potential SERS supports, which illustrate the vibrational properties of the reused catalyst. The reuse of the TiO2/RGO blends after the first cycle of AC photodegradation indicated their suitable stability during the five cycles of pharmaceutical compound photodegradation. [ABSTRACT FROM AUTHOR]

In this article, we review recent progress concerning the development of sensorial platforms based on graphene derivatives and conducting polymers (CPs), alternatively deposited or co-deposited on the working electrode (usually a glassy carbon electrode; GCE) using a simple potentiostatic method (often cyclic voltammetry; CV), possibly followed by the deposition of metallic nanoparticles (NPs) on the electrode surface (ES). These materials have been successfully used to detect an extended range of biomolecules of clinical interest, such as uric acid (UA), dopamine (DA), ascorbic acid (AA), adenine, guanine, and others. The most common method is electrochemical synthesis. In the composites, which are often combined with metallic NPs, the interaction between the graphene derivatives—including graphene oxide (GO), reduced graphene oxide (RGO), or graphene quantum dots (GQDs)—and the CPs is usually governed by non-covalent functionalization through π–π interactions, hydrogen bonds, and van der Waals (VW) forces. The functionalization of GO, RGO, or GQDs with CPs has been shown to speed up electron transfer during the oxidation process, thus improving the electrochemical response of the resulting sensor. The oxidation mechanism behind the electrochemical response of the sensor seems to involve a partial charge transfer (CT) from the analytes to graphene derivatives, due to the overlapping of π orbitals. [ABSTRACT FROM AUTHOR]

In this work, new results concerning the potential of mixtures based on nitrogen doped titanium dioxide (TiO2:N) and carbon nanotubes (CNTs) as possible catalyst candidates for the rhodamine B (RhB) UV photodegradation are reported. The RhB photodegradation was evaluated by UV–VIS absorption spectroscopy using samples of TiO2:N and CNTs of the type of single-walled carbon nanotubes (SWNTs), double-wall carbon nanotubes (DWNTs), multi-wall carbon nanotubes (MWNTs), and single-walled carbon nanotubes functionalized with carboxyl groups (SWNT-COOH) having various concentrations of CNTs. The best photocatalytic performance was obtained for sample containing TiO2:N and 2.5 wt.% SWNTs-COOH, when approx. 85% of dye removal was achieved after 300 min. of UV irradiation. The reaction kinetics of RhB aqueous solutions containing TiO2:N/CNT mixtures followed a complex first-order kinetic model. The TiO2:N/CNTs catalyst induced higher photodegradation efficiency of RhB than TiO2:N due to the presence of CNTs, which act as adsorbent and dispersing agent and capture the photogenerated electrons of TiO2:N hindering the electron–hole recombination. [ABSTRACT FROM AUTHOR]

In this study, we provide the reader with an overview of quantum dot application in solar cells to replace dye molecules, where the quantum dots play a key role in photon absorption and excited charge generation in the device. The brief shows the types of quantum dot sensitized solar cells and presents the obtained results of them for each type of cell, and provides the advantages and disadvantages. Lastly, methods are proposed to improve the efficiency performance in the next researching. [ABSTRACT FROM AUTHOR]

Multifunctional Bi- and Fe-modified carbon xerogel composites (CXBiFe), with different Fe concentrations, were obtained by a resorcinol–formaldehyde sol–gel method, followed by drying in ambient conditions and pyrolysis treatment. The morphological and structural characterization performed by X-ray diffraction (XRD), Raman spectroscopy, N2 adsorption/desorption porosimetry, scanning electron microscopy (SEM) and scanning/transmission electron microscopy (STEM) analyses, indicates the formation of carbon-based nanocomposites with integrated Bi and Fe oxide nanoparticles. At higher Fe concentrations, Bi-Fe-O interactions lead to the formation of hybrid nanostructures and off-stoichiometric Bi2Fe4O9 mullite-like structures together with an excess of iron oxide nanoparticles. To examine the effect of the Fe content on the electrochemical performance of the CXBiFe composites, the obtained powders were initially dispersed in a chitosan solution and applied on the surface of glassy carbon electrodes. Then, the multifunctional character of the CXBiFe systems is assessed by involving the obtained modified electrodes for the detection of different analytes, such as biomarkers (hydrogen peroxide) and heavy metal ions (i.e., Pb2+). The achieved results indicate a drop in the detection limit for H2O2 as Fe content increases. Even though the current results suggest that the surface modifications of the Bi phase with Fe and O impurities lower Pb2+ detection efficiencies, Pb2+ sensing well below the admitted concentrations for drinkable water is also noticed. [ABSTRACT FROM AUTHOR]

This work is devoted to the study of phase transition processes in nanostructured ceramics of the Y2O3/TiO2-Y2TiO5 type doped with carbon nanotubes as a result of thermal annealing, as well as to the assessment of the prospects of the effect of phase composition on photocatalytic activity. By the method of X-ray phase analysis, it was found that an increase in the annealing temperature leads to the formation of the orthorhombic phase Y2TiO5, as well as structural ordering. Based on the obtained UV spectra, the band gap was calculated, which varies from 2.9 eV (initial sample) to 2.1 eV (annealed at a temperature of 1000 °C). During photocatalytic tests, it was established that the synthesized nanostructured ceramics Y2O3/TiO2-Y2TiO5 doped CNTs show a fairly good photocatalytic activity in the range of 60–90% decomposition of methyl orange. [ABSTRACT FROM AUTHOR]