Search

Reasonably regulating electronic coupling to promote charge transfer and exciton separation has been regarded a promising approach in catalysis. The material engineering of van der Waals heterojunction (vdWsH) based on two-dimensional (2D) materials would be a potential way to optimize the as-prepared extrinsic physicochemical characteristics. However, it was still an almost uncultivated land waiting for exploration in catalysis. Herein, we introduced the inert h-boron nitride (h-BN) in non-metal reduced graphene oxide (GN) catalysts and constructed BN-GN vdWsH. The theoretical calculation demonstrated that the h-BN can effectively modify the electronic properties of graphene. With the introduction of h-BN, the BN-GN vdWsH can obviously enhance the catalytic activity of Li-CO2 battery. The existence of BN-GN vdWsH can reduce the overpotential more than 700 mV compared with reduced graphene oxide during the CO2 reduction reaction (CO2RR) and CO2 evolution reaction (CO2ER), and it extended cyclic stability more than three times, which was one of the most outstanding non-metallic catalysts. The reasonable structure design made it work as a high efficient electrocatalyst, which shed light on the development for functional treatment of catalytic materials.

Lithium-oxygen batteries have attracted considerable interest in the past a few years, because they have higher theoretical specific energy than Li-ion batteries. However, the available energy densities of the Li-O2 batteries are much less than expected. It is particularly urgent to find catalyst with high activity. Herein, a series of Co3O4 with different morphologies (ordered two-dimensional porous nanosheets, flowerlike and cuboidlike) were successfully prepared through facile hydrothermal and calcination methods. Ordered two-dimensional Co3O4 nanosheets show the best cycling stability. Detailed experimental results reveal that the superiority of the unique two-dimensional uniform porous structures is vital for Li-O2 batteries cathode catalysts. Due to the ordered structures with high surface areas and active sites, the catalysts indicate a high specific discharge capacity of about 10,417 mAh/g at a current density of 200 mA/g, and steadily cycle for more than 50 times with a limited capacity of 1,000 mAh/g.

A novel two-phase approach towards the corrosion of PtNi10 nanoctahedra has been developed. In this strategy, the active component of Ni in oil-soluble PtNi10 nanoctahedra which resided in the upper toluene phase, suffered from etching and was then transferred into a lower aqueous phase with coordination by ethylenediaminetetraacetate (EDTA). Due to the existence of the phase-transfer interface promoted by EDTA, the corrosion reaction proceeded at an accelerated rate under the mild conditions. Specifically, the resultant products of octahedral Pt4Ni nanoframes were successfully fabricated for the first time, and PtNi4 porous octahedra could be obtained when the dosage of EDTA-2Na was reduced. After a systematic study of this two-phase system, a “synergetic corrosion” mechanism is proposed to account for the formation of octahedral Pt4Ni nanoframes, involving contributions from many species (i.e., O2, H2O, H+, OAm, and EDTA4−). As a result of the fascinating three-dimensional geometry of Pt4Ni nanoframes and PtNi4 porous octahedra, both of the corroded nanocrystals showed superior activity over the pristine PtNi10 nanoctahedra for ethanol electrooxidation in alkaline media and hydrogenation of nitrobenzene.

Lithium iron phosphate (LiFePO4) is a potential high efficiency cathode material for lithium ion batteries, but the low electronic conductivity and single diffusion channel for lithium ions require good particle size and shape control during the synthesis of this material. In this paper, six LiFePO4 nanocrystals with different size and shape have been successfully synthesized in ethylene glycol. The addition sequence Fe-PO4-Li helps to form LiFePO4 nanocrystals with mostly {010} faces exposed, and increasing the amount of LiOH leads to a decrease in particle size. The electrochemical performance of the six distinct LiFePO4 particles show that the most promising LiFePO4 nanocrystals either have predominant {010} face exposure or high specific area, with little iron(II) oxidation.

[020]-oriented tin sulfide nanobelts with a length/thickness ratio of 100 have been synthesized by a facile hydrothermal method without any surfactants, and the nanobelts have shown good strain-accommodating properties as well as good electrochemical performance as the anode for Li-ion batteries. The formation of the nanobelts results from a precipitation-dissolution-transformation mechanism, and the [020] oriented growth can be ascribed to the {010} facet family having the lowest atomic density. In particular, SnS shows clear Li-Sn alloying/de-alloying reversible reactions in the potential range 0.1–1.0 V. Based on galvanostatic measurements and electrochemical impedance spectroscopy, SnS nanobelts have shown impressive rate performance. The post-cycled SnS nanobelts were completely transformed into metallic tin, and preserved the one-dimensional structure due to their flexibility which accommodates the large volumetric expansion. Open image in new window