In the orthopedic and dental fields, simultaneously conferring titanium (Ti) and its alloy implants with antibacterial and bone-bonding capabilities is an outstanding challenge. In the present study, we developed a novel combined solution and heat treatment that controllably incorporates 0.7% to 10.5% of iodine into Ti and its alloys by ion exchange with calcium ions in a bioactive calcium titanate. The treated metals formed iodine-containing calcium-deficient calcium titanate with abundant Ti-OH groups on their surfaces. High-resolution XPS analysis revealed that the incorporated iodine ions were mainly positively charged. The surface treatment also induced a shift in the isoelectric point toward a higher pH, which indicated a prevalence of basic surface functionalities. The Ti loaded with 8.6% iodine slowly released 5.6 ppm of iodine over 90 days and exhibited strong antibacterial activity (reduction rate &gt, 99%) against methicillin-resistant Staphylococcus aureus (MRSA), S. aureus, Escherichia coli, and S. epidermidis. A long-term stability test of the antibacterial activity on MRSA showed that the treated Ti maintained a &gt, 99% reduction until 3 months, and then it gradually decreased after 6 months (to a 97.3% reduction). There was no cytotoxicity in MC3T3-E1 or L929 cells, whereas apatite formed on the treated metal in a simulated body fluid within 3 days. It is expected that the iodine-carrying Ti and its alloys will be particularly useful for orthopedic and dental implants since they reliably bond to bone and prevent infection owing to their apatite formation, cytocompatibility, and sustainable antibacterial activity.

Selective laser melting (SLM) is a promising technology capable of producing individual characteristics with a high degree of surface roughness for implants. These surfaces can be modified so as to increase their osseointegration, bone generation and biocompatibility, features which are critical to their clinical success. In this study, we evaluated the effects on preosteoblast proliferation and differentiation of titanium metal (Ti) with a high degree of roughness (Ra = 5.4266 ± 1.282 µm) prepared by SLM (SLM-Ti) that was also subjected to surface bioactive treatment by mixed acid and heat (MAH). The results showed that the MAH treatment further increased the surface roughness, wettability and apatite formation capacity of SLM-Ti, features which are useful for cell attachment and bone bonding. Quantitative measurement of osteogenic-related gene expression by RT-PCR indicated that the MC3T3-E1 cells on the SLM-Ti MAH surface presented a stronger tendency towards osteogenic differentiation at the genetic level through significantly increased expression of Alp, Ocn, Runx2 and Opn. We conclude that bio-activated SLM-Ti enhanced preosteoblast differentiation. These findings suggest that the mixed acid and heat treatment on SLM-Ti is promising method for preparing the next generation of orthopedic and dental implants because of its apatite formation and cell differentiation capability.