Search

Among photodetectors, avalanche photodiodes (APDs) have an important place due to their excellent sensitivity to light. APDs transform photons into electrons and then multiply the electrons, leading to an amplified photocurrent. APDs are promising for faint light detection owing to this outstanding advantage, which will boost LiDAR applications. Although Si APDs have already been commercialized, their spectral region is very limited in many applications. Therefore, it is urgently demanded that the spectral region APDs be extended to the short-wavelength infrared (SWIR) region, which means better atmospheric transmission, a lower solar radiation background, a higher laser eye safety threshold, etc. Up until now, both Ge (GeSn) and InGaAs were employed as the SWIR absorbers. The aim of this review article is to provide a full understanding of Ge(GeSn) and InGaAs for PDs, with a focus on APD operation in the SWIR spectral region, which can be integrated onto the Si platform and is potentially compatible with CMOS technology. [ABSTRACT FROM AUTHOR]

The realization of high-performance Si-based III-V quantum-dot (QD) lasers has long attracted extensive interest in optoelectronic circuits. This manuscript presents InAs/GaAs QD lasers integrated on an advanced GaAs virtual substrate. The GaAs layer was originally grown on Ge as another virtual substrate on Si wafer. No patterned substrate or sophisticated superlattice defect-filtering layer was involved. Thanks to the improved quality of the comprehensively modified GaAs crystal with low defect density, the room temperature emission wavelength of this laser was allocated at 1320 nm, with a threshold current density of 24.4 A/cm−2 per layer and a maximum single-facet output power reaching 153 mW at 10 °C. The maximum operation temperature reaches 80 °C. This work provides a feasible and promising proposal for the integration of an efficient O-band laser with a standard Si platform in the near future. [ABSTRACT FROM AUTHOR]

GeSn alloys have already attracted extensive attention due to their excellent properties and wide-ranging electronic and optoelectronic applications. Both theoretical and experimental results have shown that direct bandgap GeSn alloys are preferable for Si-based, high-efficiency light source applications. For the abovementioned purposes, molecular beam epitaxy (MBE), physical vapour deposition (PVD), and chemical vapor deposition (CVD) technologies have been extensively explored to grow high-quality GeSn alloys. However, CVD is the dominant growth method in the industry, and it is therefore more easily transferred. This review is focused on the recent progress in GeSn CVD growth (including ion implantation, in situ doping technology, and ohmic contacts), GeSn detectors, GeSn lasers, and GeSn transistors. These review results will provide huge advancements for the research and development of high-performance electronic and optoelectronic devices. [ABSTRACT FROM AUTHOR]

This article presents a novel method to grow a high-quality compressive-strain Ge epilayer on Si using the selective epitaxial growth (SEG) applying the RPCVD technique. The procedures are composed of a global growth of Ge layer on Si followed by a planarization using CMP as initial process steps. The growth parameters of the Ge layer were carefully optimized and after cycle-annealing treatments, the threading dislocation density (TDD) was reduced to 3 × 107 cm−2. As a result of this process, a tensile strain of 0.25% was induced, whereas the RMS value was as low as 0.81 nm. Later, these substrates were covered by an oxide layer and patterned to create trenches for selective epitaxy growth (SEG) of the Ge layer. In these structures, a type of compressive strain was formed in the SEG Ge top layer. The strain amount was −0.34%; meanwhile, the TDD and RMS surface roughness were 2 × 106 cm−2 and 0.68 nm, respectively. HRXRD and TEM results also verified the existence of compressive strain in selectively grown Ge layer. In contrast to the tensile strained Ge layer (globally grown), enhanced PL intensity by a factor of more than 2 is partially due to the improved material quality. The significantly high PL intensity is attributed to the improved crystalline quality of the selectively grown Ge layer. The change in direct bandgap energy of PL was observed, owing to the compressive strain introduced. Hall measurement shows that a selectively grown Ge layer possesses room temperature hole mobility up to 375 cm2/Vs, which is approximately 3 times larger than that of the Ge (132 cm2/Vs). Our work offers fundamental guidance for the growth of high-quality and compressive strain Ge epilayer on Si for future Ge-based optoelectronics integration applications. [ABSTRACT FROM AUTHOR]

In this article, we demonstrated novel methods to improve the performance of p-i-n photodetectors (PDs) on a germanium-on-insulator (GOI). For GOI photodetectors with a mesa diameter of 10 μm, the dark current at −1 V is 2.5 nA, which is 2.6-fold lower than that of the Ge PD processed on Si substrates. This improvement in dark current is due to the careful removal of the defected Ge layer, which is formed with the initial growth of Ge on Si. The bulk leakage current density and surface leakage density of the GOI detector at −1 V are as low as 1.79 mA/cm2 and 0.34 μA/cm, respectively. GOI photodetectors with responsivity of 0.5 and 0.9 A/W at 1550 and 1310 nm wavelength are demonstrated. The optical performance of the GOI photodetector could be remarkably improved by integrating a tetraethylorthosilicate (TEOS) layer on the oxide side due to the better optical confinement and resonant cavity effect. These PDs with high performances and full compatibility with Si CMOS processes are attractive for applications in both telecommunications and monolithic optoelectronics integration on the same chip. [ABSTRACT FROM AUTHOR]

The international technology roadmap of semiconductors (ITRS) is approaching the historical end point and we observe that the semiconductor industry is driving complementary metal oxide semiconductor (CMOS) further towards unknown zones. Today's transistors with 3D structure and integrated advanced strain engineering differ radically from the original planar 2D ones due to the scaling down of the gate and source/drain regions according to Moore's law. This article presents a review of new architectures, simulation methods, and process technology for nano-scale transistors on the approach to the end of ITRS technology. The discussions cover innovative methods, challenges and difficulties in device processing, as well as new metrology techniques that may appear in the near future. [ABSTRACT FROM AUTHOR]