In this work, nitrogen-doped porous biochars were synthesized from spruce bark waste using a facile single-step synthesis process, with H3PO4 as the chemical activator. The effect of nitrogen doping on the carbon material's physicochemical properties and adsorption ability to adsorb the Reactive Orange 16 dye and treat synthetic effluents containing dyes were evaluated. N doping did not cause an important impact on the specific surface area values, but it did cause an increase in the microporosity (from 19% to 54% of micropores). The effect of the pH showed that the RO-16 reached its highest removal level in acidic conditions. The kinetic and equilibrium data were best fitted by the Elovich and Redlich–Peterson models, respectively. The adsorption capacities of the non-doped and doped carbon materials were 100.6 and 173.9 mg g−1, respectively. Since the biochars are highly porous, pore filling was the main adsorption mechanism, but other mechanisms such as electrostatic, hydrogen bond, Lewis acid-base, and π-π between mechanisms were also involved in the removal of RO-16 using SB-N-Biochar. The adsorbent biochar materials were used to treat synthetic wastewater containing dyes and other compounds and removal efficiencies of up to 66% were obtained. The regeneration tests have demonstrated that the nitrogen-doped biochar could be recycled and reused easily, maintaining very good adsorption performance even after five cycles. This work has demonstrated that N-doped biochar is easy to prepare and can be employed as an efficient adsorbent for dye removal, helping to open up new solutions for developing sustainable and effective adsorption processes to tackle water contamination. [ABSTRACT FROM AUTHOR]

This work reports the successful preparation of nanoporous iron oxide/carbon composites through the in-situ growth of Prussian blue (PB) nanoparticles on the surface of graphene oxide (GO) nanosheets. The applied thermal treatment allows the conversion of PB nanoparticles into iron oxide (Fe2O3) nanoparticles. The resulting iron oxide/carbon composite exhibits higher specific capacitance at all scan rates than pure GO and Fe2O3 electrodes due to the synergistic contribution of electric double-layer capacitance from GO and pseudocapacitance from Fe2O3. Notably, even at a high current density of 20 A g−1, the iron oxide/carbon composite still shows a high capacitance retention of 51%, indicating that the hybrid structure provides a highly accessible path for diffusion of electrolyte ions. [ABSTRACT FROM AUTHOR]