Polydopamine (PDA)—a known adhesive coating material—was used herein to strongly immobilize a Pt-particle catalyst on an acrylonitrile–butadiene–styrene copolymer (ABS) substrate. Previous studies have shown that the poor adhesion between Pt particles and ABS surfaces is a considerable problem, leading to low catalytic durability for H2O2 decomposition during contact-lens cleaning. First, the ABS substrate was coated with PDA, and the PDA film was evaluated by X-ray photoelectron spectroscopy. Second, Pt particles were immobilized on the PDA-coated ABS substrate (ABS-PDA) using the electron-beam irradiation reduction method. The Pt particles immobilized on ABS-PDA (Pt/ABS-PDA) were observed using a scanning electron microscope. The Pt-loading weight was measured by inductively coupled plasma atomic emission spectroscopy. Third, the catalytic activity of the Pt/ABS-PDA was evaluated as the residual H2O2 concentration after immersing it in a 35,000-ppm H2O2 solution (the target value was less than 100 ppm). The catalytic durability was evaluated as the residual H2O2 concentration after repeated use. The PDA coating drastically improved both the catalytic activity and durability because of the high Pt-loading weight and strong adhesion among Pt particles, PDA, and the ABS substrate. Plasma treatment prior to PDA coating further improved the catalytic durability. [ABSTRACT FROM AUTHOR]

In a previous study, Pt nanoparticles were supported on a substrate of acrylonitrile–butadiene–styrene copolymer (ABS) to give the ABS surface catalytic activity for H2O2 decomposition during contact lens cleaning. Although the Pt-particle/ABS catalysts exhibited considerably high specific catalytic activity for H2O2 decomposition, the catalytic activity decreased with increasing numbers of repeated usage, which meant the durability of the catalytic activity was low. Therefore, to improve the catalytic durability in this study, we proposed two types of pretreatments, as well as a combination of these treatments before supporting Pt nanoparticles on the ABS substrate. In the first method, the ABS substrate was etched, and in the second method, the surface charge of the ABS substrate was controlled. A combination of etching and surface charge control was also applied as a third method. The effects of these pretreatments on the surface morphology, surface chemical composition, deposition behavior of Pt particles, and Pt loading weight were investigated by scanning electron microscopy (SEM), X-ray photoelectron spectroscopy (XPS), cross-sectional SEM, and inductively coupled plasma atomic emission spectroscopy (ICP-AES), respectively. Both etching and controlling the surface charge effectively improved the catalytic durability for H2O2 decomposition. In addition, the combination treatment was the most effective. [ABSTRACT FROM AUTHOR]