Introduction of surface defects and phase control engineering in the electrocatalytic system of overall water splitting has played a crucial role in significantly enhancing its electrocatalytic activity toward the hydrogen evolution reaction (HER) and the oxygen evolution reaction (OER) in water splitting, but the relationship between structure and electrocatalysis is still elusive. Herein, we report a solid–liquid method to induce surface reorganization (formation of a chalcogenide layer with rich chalcogenide vacancies) and phase transformation (Co9S8-to-Co3S4) simultaneously on cobalt chalcogenide. Featuring a uniform 2D morphology and the in situ formation of sulfur (S) vacancies, in a 0.1 M KOH solution, it exhibits a low overpotential of 288 mV vs. RHE at 10 mA cm−2, a low Tafel slope of 43.4 mV dec−1, and strong cycling stability (35 h), outperforming commercial RuO2 and most reported OER electrocatalysts. In addition, we also investigate the OER activity of the Co–S–P electrode in 1.0 M KOH solutions. Co0.37S0.38P0.02 NSs only need 257 mV to reach a current density of 10 mA cm−2. Meanwhile, the Tafel slope of Co0.37S0.38P0.02 NSs (44.0 mV dec−1) is lower than those of other recently reported electrocatalysts. Also, it shows high HER electrocatalytic activity in alkaline and acidic solutions. Finally, the Co0.37S0.38P0.02 electrode is used as a cathode and anode simultaneously for overall water splitting, which merely requires a cell voltage of 1.59 V at 10 mA cm−2 with excellent stability (40 h).

Defect engineering is widely applied in transition metal dichalcogenides to produce high-purity hydrogen. However, the instability of vacancy states on catalysis still remains a considerable challenge. Here, our first-principles calculations showed that, by optimizing the asymmetric S vacancy in the highly asymmetric 1T' crystal of layered bitransition metal dichalcogenides (Co-MoS2) in light of Pd modulation, the relative amount of metastable phase and the quantity of active sites in the structure can be reduced and increased, respectively, leading to a further boosted hydrogen evolution reaction (HER) activity toward layered bi-transition metal dichalcogenides. Thus, we then used a "click" chemistry strategy to make such a catalyst with engineered unsaturated sulfur edges via a strong coupling effect between ultrafine Pd ensembles and Co-MoS2 nanosheets. As expected, the Pd-modulated Co-MoS2 nanosheets exhibited a very low overpotential of 60 mV at 10 mA cm-2 with a small Tafel slope (56 mV dec-1) for the HER in 1.0 M PBS, comparable to those of commercial Pt/C. In addition, their high HER activity was retained in acidic and alkaline conditions. Both the theoretical and experimental results revealed that Pd ensembles can efficiently activate and stabilize the inert basal plane S sites during HER processes as a result of the formation of Pd-S in Co-MoS2. This work not only provides a deeper understanding of the correlation between defect sites and intrinsic HER catalytic properties for transition metal chalcogenide (TMD)-based catalysts, but also offers new insights into better designing earth-abundant HER catalysts displaying high efficiency and durability.