Abstract We report on bifurcate reactions on the surface of well-aligned Si1−xGex nanowires that enable fabrication of two different coaxial heterostructure nanowires. The Si1−xGex nanowires were grown in a chemical vapor transport process using SiCl4 gas and Ge powder as a source. After the growth of nanowires, SiCl4 flow was terminated while O2 gas flow was introduced under vacuum. On the surface of nanowires was deposited Ge by the vapor from the Ge powder or oxidized into SiO2 by the O2 gas. The transition from deposition to oxidation occurred abruptly at 2 torr of O2 pressure without any intermediate region and enables selectively fabricated Ge/Si1−xGex or SiO2/Si1−xGex coaxial heterostructure nanowires. The rate of deposition and oxidation was dominated by interfacial reaction and diffusion of oxygen through the oxide layer, respectively.

Abstract Silicon nanoribbons (Si NRs) with a thickness of about 30 nm and a width up to a few micrometers were synthesized. Systematic observations indicate that Si NRs evolve via the following sequences: the growth of basal nanowires assisted with a Pt catalyst by a vapor-liquid-solid (VLS) mechanism, followed by the formation of saw-like edges on the basal nanowires and the planar filling of those edges by a vapor-solid (VS) mechanism. Si NRs have twins along the longitudinal < 110 > growth of the basal nanowires that also extend in < 112 > direction to edge of NRs. These twins appear to drive the lateral growth by a reentrant twin mechanism. These twins also create a mirror-like crystallographic configuration in the anisotropic surface energy state and appear to further drive lateral saw-like edge growth in the < 112 > direction. These outcomes indicate that the Si NRs are grown by a combination of the two mechanisms of a Pt-catalyst-assisted VLS mechanism for longitudinal growth and a twin-assisted VS mechanism for lateral growth.