Unique bimodal distributions of single crystal epitaxially grown In2O3 nanodots on silicon are shown to have excellent IR transparency greater than 87% at IR wavelengths up to 4 μm without sacrificing transparency in the visible region. These broadband antireflective nanodot dispersions are grown using a two-step metal deposition and oxidation by molecular beam epitaxy, and backscattered diffraction confirms a dominant (111) surface orientation. We detail the growth of a bimodal size distribution that facilitates good surface coverage (80%) while allowing a significant reduction in In2O3 refractive index. This unique dispersion offers excellent surface coverage and three-dimensional volumetric expansion compared to a thin film, and a step reduction in refractive index compared to bulk active materials or randomly porous composites, to more closely match the refractive index of an electrolyte, improving transparency. The (111) surface orientation of the nanodots, when fully ripened, allows minimum lattice mismatch strain between the In2O3 and the Si surface. This helps to circumvent potential interfacial weakening caused by volume contraction due to electrochemical reduction to lithium, or expansion during lithiation. Cycling under potentiodynamic conditions shows that the transparent anode of nanodots reversibly alloys lithium with good Coulombic efficiency, buffered by co-insertion into the silicon substrate. These properties could potentially lead to further development of similarly controlled dispersions of a range of other active materials to give transparent battery electrodes or materials capable of non-destructive in situ spectroscopic characterization during charging and discharging. [ABSTRACT FROM AUTHOR]

The surface orientation of metal nanoparticles is critical to their physical and chemical properties. This study aims on the understanding of the effect of surface orientation as well as heterogeneous epitaxy of metal nanoparticles at an interface between two materials with a large lattice mismatch. Silver nanoparticles of different diameters were grown on arrays of calcium fluoride (CaF2) nanorods using oblique angle deposition as a model system for this study. Scanning electron microscopy and transmission electron microscopy (TEM) imaging were used to verify that the nanoparticles were selectively grown on the desired {111} facets of the nanorod tips. Using selected area diffraction and dark field imaging in TEM, it was shown that the nanoparticles were grown at a (111) orientation at the CaF2 interface with large lattice strains. Thus biaxially textured CaF2 nanorod arrays can be used as a catalytic support. [ABSTRACT FROM AUTHOR]