Search

Atomic-force microscopic images, x-ray diffraction patterns, Urbach energies and photoluminescence quenching experiments show that the interfacial contact quality between the hydrophobic [6,6]-phenyl-C61-buttric acid methyl ester (PCBM) thin film and hydrophilic CH3NH3PbI3 (MAPbI3) thin film can be effectively improved by using a binary antisolvent mixture (toluene:dichloromethane or chlorobenzene:dichloromethane) in the anti-solvent mixture-mediated nucleation process, which increases the averaged power conversion efficiency of the resultant PEDOT:PSS (P3CT-Na) thin film based MAPbI3 solar cells from 13.18% (18.52%) to 13.80% (19.55%). Beside, the use of 10% dichloromethane (DCM) in the binary antisolvent mixture results in a nano-textured MAPbI3 thin film with multicrystalline micrometer-sized grains and thereby increasing the short-circuit current density and fill factor (FF) of the resultant solar cells. It is noted that a remarkable FF of 80.33% is achieved, which can be used to explain the stable photovoltaic performance without additional encapsulations. [ABSTRACT FROM AUTHOR]

The averaged power conversion efficiency of polyelectrolytes (P3CT-Na) based MAPbI3 solar cells can be increased from 14.94% to 17.46% with a wetting method before the spin-coating process of MAPbI3 precursor solutions. The effects of the wetting process on the surface, structural, optical and excitonic properties of MAPbI3 thin films are investigated by using the atomic-force microscopic images, x-ray diffraction patterns, transmittance spectra, photoluminescence spectra and Raman scattering spectra. The experimental results show that the wetting process of MAPbI3 precursor solution on top of the P3CT-Na/ITO/glass substrate can be used to manipulate the molecular packing structure of the P3CT-Na thin film, which determines the formation of MAPbI3 thin films. [ABSTRACT FROM AUTHOR]

A graded fullerene derivative thin film was used as a dual-functional electron transport layer (ETL) in CH3NH3PbI3 (MAPbI3) solar cells, to improve the fill factor (FF) and device stability. The graded ETL was made by mixing phenyl-C61-butyric acid methyl ester (PCBM) molecules and C60-diphenylmethanofullerene-oligoether (C60-DPM-OE) molecules using the spin-coating method. The formation of the graded ETLs can be due to the phase separation between hydrophobic PCBM and hydrophilic C60-DPM-OE, which was confirmed by XPS depth-profile analysis and an electron energy-loss spectroscope. Comprehensive studies were carried out to explore the characteristics of the graded ETLs in MAPbI3 solar cells, including the surface properties, electronic energy levels, molecular packing properties and energy transfer dynamics. The elimination of the s-shape in the current density–voltage curves results in an increase in the FF, which originates from the smooth contact between the C60-DPM-OE and hydrophilic MAPbI3 and the formation of the more ordered ETL. There was an improvement in device stability mainly due to the decrease in the photothermal induced morphology change of the graded ETLs fabricated from two fullerene derivatives with distinct hydrophilicity. Consequently, such a graded ETL provides dual-functional capabilities for the realization of stable high-performance MAPbI3 solar cells. [ABSTRACT FROM AUTHOR]