In the Large Helical Device (LHD), the first deuterium plasma experiment was conducted in 2017. To investigate tritium migration in the LHD vacuum vessel, long-term material probes were installed on the first wall before the deuterium plasma experiment. After the experiment, the microstructure and amount of tritium remaining in each probe were analyzed. The results showed that a relatively large amount of tritium remained in the probes on the first wall, forming a thick deposition layer, rather than in the probes located in the erosion-dominant area. In the deposition layers on the probes, the dominant element is carbon, which can be generated on the divertor tiles made of graphite. The result of orbit calculation of the energetic tritons in the case of the standard magnetic configuration in the LHD showed that approximately 40% of the tritons generated by deuterium–deuterium fusion reactions were promptly lost mainly to the divertor. Thermalized tritons also flew to the divertor along with the background plasma. The divertor tiles, on which the tritons impinged, were eroded by the divertor plasma, and carbon atoms and tritiated hydrocarbon molecules were generated and deposited on the first wall. This can be the dominant mechanism of tritium retention in the first wall. Among the material probes located in the erosion-dominant area, the amount of tritium remaining in the probe on which the energetic tritons impinged was relatively large. The results of the tritium balance analysis show that the first wall is not the dominant reservoir of tritium in the LHD.

Poly-crystalline tungsten (W) samples were simultaneously irradiated with Helium (He) and Deuterium (D) ions using the triple-ion implantation device. He effect on D retention and transportation was studied using different combination of ion energies and He/D flux ratios in the simultaneous implantation. The experimental results show that D trapping at dislocation loops is significantly reduced in the case of 3 keV He+–3 keV D2+at He/D flux ratios over 0.6. D trapping by stronger trapping sites such as vacancies and vacancy clusters showed less dependence on the flux ratio. On the contrary, the D retention increases at each He/D flux ratio in the case of 3 keV He+–1 keV D2+compared to only D2+ implantation even the He/D flux ratio reaches a value of 1.0. TEM observations confirmed that dense dislocation loops are formed rather than He bubbles, which is responsible for the enhanced D retention in W. Keywords: Simultaneous implantation, D retention, Helium, Flux ratio, Transportation, Thermal desorption spectroscopy

The objective of this study is to investigate the effects of neutron (n) irradiation on hydrogen isotope transport in tungsten (W). W samples were irradiated with neutrons in a fission reactor and then exposed to high flux deuterium (D) plasma at 563 K in a linear plasma device. The fraction of D release increased with increasing exposure time. In addition, the D retention in n-irradiated W increased in proportion to the square root of the plasma exposure time. These observations were explained by increase in the penetration depth of D with filling up displacement damages acting as strong trapping sites.