Search

Ho,Pr:CaYAlO 4 (Ho,Pr:CYA) crystal doped with 1 at.% Ho3+ and 0.1 at.% Pr3+ was successfully grown using the Czochralski method. Polarized absorption spectra, emission spectra, and fluorescence lifetime measurements were performed. The impact of Pr3+ co-doping on the ∼3 μm emission of Ho3+ ions was analyzed. The energy transfer efficiency from Ho3+:5I 7 to Pr3+:3F 2 energy level was calculated to be 60.66 %, indicating that Pr3+ effectively mitigated the self-termination effect in Ho,Pr:CYA crystals. The absorption cross-section at 645 nm was found to be 1.53 × 10−20 cm2 for σ polarization and 2.62 × 10−20 cm2 for π polarization. The emission cross-section at 2842 nm was calculated to be 0.86 × 10−20 cm2 for σ polarization and 1.33 × 10−20 cm2 for π polarization at 2908 nm, with a full width at half maximum (FWHM) of 139 nm and 88 nm, respectively. The fluorescence lifetimes of the 5I 6 and 5I 7 levels were measured to be 0.17 ms and 2.01 ms, respectively. These results collectively suggest that Ho,Pr:CYA crystals hold great potential as a candidate for 2.8 μm laser applications. • Ho3+,Pr3+ co-doped CaYAlO 4 crystal was grown by the Czochralski method. • The crystal structure, polarized absorption and emission spectra were investigated. • The intensity parameters were obtained using J-O theory. [ABSTRACT FROM AUTHOR]

Abstract: The Cr(0.1%),Yb(10%):GGG crystals have been grown by the Czochralski method. The chemical composition is: Yb0.33Gd2.47Cr0.005Ga5.2O12. There are no observed Yb3+ ions substituting Ga3+ ions, just like that of Yb:GGG crystals. The defects in Cr,Yb:GGG crystal were also investigated. The absorption and emission spectra of Cr,Yb:GGG crystal at room temperature have been measured. The O2 and H2 annealing effect of Cr,Yb:GGG crystal have been compared. Cr3+ can greatly weak the visible luminescence of this crystal. The Cr–Yb-codoped crystals may be potential materials for compact, efficient, high stability LD pumped solid state lasers. [Copyright &y& Elsevier]

Sm:YAlO 3 (Sm:YAP) crystal with size of Φ28 × 80 mm3 was grown by Czochralski (Cz) method. Polarized absorption spectra and fluorescence spectra of Sm:YAP crystal were discussed for the first time. The peak emission cross-sections were calculated to be 0.80 × 10−21 cm2 (604 nm for a-polarization), 1.82 × 10−21 cm2 (604 nm for b-polarization) and 1.63 × 10−21 cm2 (610 nm for c-polarization), respectively. The Judd-Ofelt (JO) intensity parameters were calculated to be Ω 2 = 2.59 × 10−20 cm2, Ω 4 = 1.78 × 10−20 cm2 and Ω 6 = 2.98 × 10−20 cm2, respectively. The decay lifetime of 4G 5/2 energy level was measured to be 2.51 ms. All above results indicate the Sm:YAP crystal may be a potential candidate of reddish-orange laser pumped directly by the GaN/InGaN laser diode. • Sm:YAlO 3 crystal was grown by Cz method. • Polarized optical spectra of Sm:YAlO 3 crystal were investigated. • The transitions of 4G 5/2 → 6H 7/2 have the highest branching ratio value, which is suitable for reddish-orange laser. [ABSTRACT FROM AUTHOR]

Abstract We report on the growth, spectroscopic properties and visible laser operation of Pr3+-doped LaMgAl 11 O 19 (LMA) crystal. The absorption and emission spectra were recorded in visible wavelength range and the decay time of 3P 0 manifold was measured to be about 34.5 μs at room temperature. Using an InGaN laser diode as pump source, continuous-wave laser operation of Pr:LMA crystal have also been demonstrated in red at about 645 nm and deep red at about 725 nm, which provide new linearly polarized sources for various potential applications. Highlights • A Pr:LMA crystal was successfully gown by using the Czochralski method. • Spectral parameters of Pr:LMA crystal were obtained. • Using a blue laser diode as pump source, red and deep red laser were demonstrated from Pr:LMA crystal. [ABSTRACT FROM AUTHOR]

Dy 3+ -doped YAlO 3 single crystal has been successfully grown by Czochralski technique. The spectroscopic parameters were determined by Judd-Ofelt theory based on the measured polarized absorption spectra. Dy:YAP crystal exhibits a yellow emission centered at 574 nm which can be used for pumping of the forbidden 1 S 0 - 3 P 0 ytterbium clock transition. The decay lifetime of the 4 F 9/2 level was measured to be 185 μs. [ABSTRACT FROM AUTHOR]