Search

The crystal growth, optical spectra and lifetime of Dy:CaGdAlO 4 crystal were investigated for the first time to our best knowledge. Single Dy:CaGdAlO 4 crystal with size of Φ4 × 40 mm 3 was grown by floating zone method. The peak absorption cross-sections were calculated to be 2.43 × 10 −21 cm 2 and 1.28 × 10 −21 cm 2 at 453 nm for σ and π polarizations. The Judd-Ofelt (JO) parameters of Ω 2 , Ω 4 and Ω 6 were calculated to be 1.8 × 10 −20 cm 2 , 1.0 × 10 −20 cm 2 and 0.5 × 10 −20 cm 2 , respectively. The emission cross-sections were calculated to be 0.51 × 10 −20 cm 2 and 0.55 × 10 −20 cm 2 for σ and π polarizations. The fluorescence decay time is 222 μs. The results indicate that the Dy:CaGdAlO 4 crystal is a potential candidate for yellow laser operation. [ABSTRACT FROM AUTHOR]

Sm:YAlO 3 (Sm:YAP) crystal with size of Φ28 × 80 mm3 was grown by Czochralski (Cz) method. Polarized absorption spectra and fluorescence spectra of Sm:YAP crystal were discussed for the first time. The peak emission cross-sections were calculated to be 0.80 × 10−21 cm2 (604 nm for a-polarization), 1.82 × 10−21 cm2 (604 nm for b-polarization) and 1.63 × 10−21 cm2 (610 nm for c-polarization), respectively. The Judd-Ofelt (JO) intensity parameters were calculated to be Ω 2 = 2.59 × 10−20 cm2, Ω 4 = 1.78 × 10−20 cm2 and Ω 6 = 2.98 × 10−20 cm2, respectively. The decay lifetime of 4G 5/2 energy level was measured to be 2.51 ms. All above results indicate the Sm:YAP crystal may be a potential candidate of reddish-orange laser pumped directly by the GaN/InGaN laser diode. • Sm:YAlO 3 crystal was grown by Cz method. • Polarized optical spectra of Sm:YAlO 3 crystal were investigated. • The transitions of 4G 5/2 → 6H 7/2 have the highest branching ratio value, which is suitable for reddish-orange laser. [ABSTRACT FROM AUTHOR]

We report on blue-diode-pumped continuous-wave Pr:YAlO 3 (YAP) crystal lasers. Using a b- cut sample, a maximum output power of 181 mW is achieved at ∼747 nm with slope efficiency of 12.7% with respect to the absorbed power. Using a c -cut sample, a dual-wavelength laser at ∼743 and ∼753 nm is obtained with a total maximum output power of 72 mW by using the blue diode pumping, for the first time to our knowledge. These laser emissions are all linearly polarized and M 2 factors of these output laser beams are also measured. YAP is experimentally verified to be one of effective oxide hosts for Pr-doped visible laser operation besides its fluoride counterparts. [ABSTRACT FROM AUTHOR]

We report on diode-pumped Nd:LuAG crystal and ceramic lasers operating at about 1.83 μm, using a simple and compact plane-concave cavity configuration. For Nd:LuAG crystal laser oscillating at 1828.43 nm, the maximum output power reaches 0.36 W with slope efficiency of about 5.0%. For Nd:LuAG ceramic laser, a maximum output power of 0.145 W is achieved with slope efficiency of about 2.2%, and the lasing wavelength peaks at 1828.76 nm. The 1.83-μm Nd laser sources could be very promising for eye-safe applications because they have stronger water absorption than another kind of eye-safe Nd lasers operating at 1.4 μm. [ABSTRACT FROM AUTHOR]

A high-quality Cr:CYA (Cr:CaYAlO 4) single crystal fiber was grown by μ-PD (Micro-Pulling-Down) method. The E//a and E//c polarized excitation spectra of Cr:CYA at room temperature was measured. The crystal field parameters were calculated and the energy level structure of Cr:CYA was analyzed. We also measured the polarization emission spectra and lifetimes at different temperatures and calculated the effective emission cross-section. Based on the above data and Boltzmann law, the thermal distribution between the excited energy levels 2E and 4A 2 at different temperatures was analyzed. The present work may be useful for guiding laser research on Cr:CYA and other Cr3+-doped laser crystals above room temperature. • Cr:CYA single crystal fiber was grown by μ-PD (Micro-Pulling-Down) method. • Excitation spectra and crystal field parameters of Cr:CYA crystals were investigated and analyzed. • The effective emission cross section of Cr:CYA at different temperatures was calculated. [ABSTRACT FROM AUTHOR]

We report a power scaled laser operation of diode-pumped Nd:LSO lasers at 1.35 μm. With single-end-pumping scheme, maximum output power reaches 0.77 W at 1358.99 nm in free-running mode. By inserting an etalon, wavelength tuning can be realized with tuning range of at least 6.5 nm from 1356.95 nm to 1363.39 nm. Simultaneous dual-wavelength laser at 1331.63 and 1357.43 nm can also be generated with total output power of 0.19 W, for the first time to our knowledge. Further power scaling to 1.03 W of the 1358.99 nm laser is finally achieved by recycling the remaining pump power, which represents the highest output power so far for 1.3 μm silicate lasers. [ABSTRACT FROM AUTHOR]

High quality 7 at%Er:Y 2 O 3 crystal was successfully grown by Fz method. Judd-Ofelt theory was applied to analyze spectroscopic properties at 2.7 μm. The larger value of Ω 2 shows low local environment symmetry exists in Er:Y 2 O 3 crystal, and the large Ω 4 /Ω 6 indicates better spectral quality. The larger absorption cross-section and FWHM are beneficial to efficient absorption of pump source. The fluorescence spectra and lifetimes of Er:Y 2 O 3 crystal were measured and studied at 2.7 μm. The emission cross-sections at 2723 nm was calculated to be 1.41 × 10−20cm2. Compared with other Er3+ doped crystals, the large spectral quality factors Q and low fluorescence lifetime ratio illustrate that Er:Y 2 O 3 crystal has excellent laser properties at 2.7 μm. In addition, the low inversion ratio also indicates great potential of Er:Y 2 O 3 crystal for laser generation at 2.7 μm. • A high quality 7%Er:Y 2 O 3 laser crystal was successfully grown by Fz method. • Judd-ofelt (J-O) parameterization scheme was applied to analyze the spectroscopic properties of 7%Er:Y 2 O 3 laser crystal at 2.7 μm. • The large spectral quality factors Q with low fluorescence lifetime ratio illustrates that Er:Y 2 O 3 crystal has excellent laser properties at 2.7 µm. • The low inversion ratio indicates great potential of Er:Y 2 O 3 crystal for laser generation at 2.7 μm. [ABSTRACT FROM AUTHOR]

Tb3+ doped Y 3 Al 5 O 12 (Tb:YAG) single crystal has been grown by the Czochralski method. Optical spectroscopic characterization of the crystal was performed in order to evaluate the potential for the visible laser application. Based on the Judd–Ofelt theory, the spectroscopic parameters Ω t (t = 2, 3, 6), spontaneous transition probabilities, fluorescence branch ratio and the radiation lifetime of excited state 5D 4 state were calculated. The green emission cross section of 5D 4 →7F 5 transition were calculated to be 1.23 × 10−21 cm2 , The yellow emission cross section of 5D 4 →7F 4 transition were calculated to be 7.08 × 10−23 cm2. The decay time of the 5D 4 level was measured to be 3.12 ms, which is in reasonable agreement with the radiation lifetime of 3.30 ms. All the results indicate the potential of Tb:YAG crystal as a visible laser material. • Tb:YAG crystal was grown by Czochralski method. • Judd-Ofelt theory was used to analyze the spectroscopic properties of Tb:YAG for the first time. • Tb:YAG crystal is a potential laser material for yellow and green laser output. [ABSTRACT FROM AUTHOR]