Search

Liquid crystal polarization gratings (LCPGs) possess unique optical properties and therefore are widely used in laser systems. Therefore, developing our understanding of the laser damage resistance of LCPGs is critical for future high-intensity laser applications. In this study, the LCPGs (Λ = 8 μm) were fabricated from liquid crystal polymer (LCP) films with photo-alignment technology, which had a small-angle (∼7.51°) diffraction order with high diffraction efficiency (∼92 %) under chiral polarized incidence at 1064 nm. The diffraction efficiency and polarization of each diffraction order were determined by the polarization of the incident light. The damage characteristics of the LCPGs were investigated using a chiral polarized nanosecond laser at 1064 nm in a one-on-one test. The laser-induced damage thresholds (LIDTs) of left-handed circular polarization (LHCP) and right-handed circular polarization (RHCP) were 8.0 J/cm2 and 8.5 J/cm2, respectively. For comparison, the LIDTs of S-polarization and P-polarization were 7.8 J/cm2 and 8.4 J/cm2, respectively. All the damage occurred at the interface between the LCP layer and the substrate when the laser fluence was near the LIDT, and the damage morphology was observed with a scanning electron microscope (SEM), including flat pits, cracks, and bumps at the edge of the pits. The results indicate that the LIDTs and damage morphology of the LCPGs were insensitive to the polarization of the irradiation. The electrical effects of differently polarized irradiation on the LCPGs were simulated using the finite element method (FEM). The electric field distribution was symmetrical under irradiation by LHCP and RHCP lasers. However, the distribution of the electric field under different linearly polarized irradiation conditions were distinct. Based on these findings, we believe that the contribution of chiral polarized irradiation to the damage was consistent and that the LIDTs were similar. This study has important implications for the application and development of LCPGs in high-intensity laser systems. • The laser-induced damage of liquid crystal polarization gratings (LCPGs) is first proposed. • We investigated the laser-induced damage of the LCPGs using a nanosecond pulsed laser with chiral polarized irradiation. • This study provides reference for the application and development of LCPGs in high-intensity laser systems. [ABSTRACT FROM AUTHOR]

Laser coatings designed for space applications not only encounter harsh space environments, but also suffer from laser irradiation. High-energy radiation in space, such as Gamma rays, can cause defects and other damage to materials, which could contribute to laser damage induced by defect absorption. In this work, we studied the optical properties and structural composition of three groups of 1064 nm multilayer antireflection (AR) coatings irradiated by Gamma rays (345 Gy), and the effect of Gamma ray radiation on the laser-induced damage properties of thin films. Experimental results revealed that after exposure to Gamma ray, the absorption and surface roughness of the AR coating increased while the transmittance decreased. X-ray photoelectron spectroscopy (XPS) analysis confirmed that SiO 2 is more fragile under Gamma radiation compared to Ta 2 O 5 and HfO 2. It was also demonstrated that the Gamma ray damage of AR coatings mainly occurred in the SiO 2 layers, and consist of generation of oxygen vacancies and charging defects. The defects generated by Gamma rays increased the absorption of the laser power by the film, hence increasing the probability of laser-induced damage and reducing the laser-induced damage threshold of the film. The coatings prepared by sputtering deposition technique showed lower probability of damage by Gamma ray radiation compared to electron-beam evaporated coatings. • The optical properties and structural composition of the 1064 nm AR coating after Gamma ray irradiation are studied. • The stability of different oxide materials prepared by different processes after Gamma irradiation is compared. • The damage of the film irradiated by Gamma rays under high-energy laser is studied. • This work provides an important reference for the development of space laser coatings. [ABSTRACT FROM AUTHOR]

Abstract: TiO2 coatings were prepared on fused silica with conventional electron beam evaporation deposition. After TiO2 thin films were annealed at different temperatures for 4h, several properties were investigated by X-ray diffraction (XRD), spectrometer, photoelectron spectroscopy (XPS) and AFM. It was found that with the annealing temperature increasing, the transmittance of TiO2 coatings decreased, and the cutoff wavelength shifted to long wavelength in near ultraviolet band. Especially, when coatings were annealed at high temperature, the optical loss is very serious, which can be attributed to the scattering and the absorption of TiO2 coatings. XRD patterns revealed that only anatase phase was observed in TiO2 coatings regardless of the different annealing temperatures. XPS results indicated that the fine chemical shift of TiO2 2p1/2 should be attributed to existence of oxygen vacancies around Ti+4 ion. The investigation on surface morphology by AFM showed that the RMS of titania thin films gradually increases from less than 0.40nm to 5.03nm and it should be ascribed to the growth of titanium dioxide grain size with the increase of annealing temperature. [Copyright &y& Elsevier]